PC/ABS LUPOY® HR5007A-KA02 LG GUANGZHOU
256
- Unit Price:
- $3402 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 63.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility High temperature resistan
- Application Areas:Electrical field Electrical components Electronic field Automotive sector Automotive interior parts
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 5.3 | g/10min |
| Melt volume flow rate | 260°C/5.0kg | ASTMD1505 | 18.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTMD955 | 0.50to0.80 | % |
| Water absorption rate | Saturation | ISO622 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-22 | 2200 | Mpa | |
| Tensile strength 2 | Yield,3.20mm,Injection | ASTMD638 | 56.9 | Mpa |
| Tensile stress | Yield | ISO527-22 | 60.0 | Mpa |
| Tensile strain | Yield | ISO527-22 | 4.9 | % |
| Tensile strain 3 | Break,3.20mm,InjectionMolded | ASTMD638 | >100 | % |
| Nominal strainatbreak | ISO527-22 | >50 | % | |
| Bending modulus 4 | 3.20mm,InjectionMolded | ASTMD790 | 2110 | Mpa |
| Bending strength 4 | 3.20mm | ASTMD790 | 77.5 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm,InjectionMolded | ASTMD648 | 113 | °C |
| 1.8MPa | ISO75-22 | 104 | °C | |
| Glass transition temperature 9 | ISO11357-22 | 150 | °C | |
| Vicat softening temperature | 50N | ISO3062 | 119 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-22 | 7.7E-05 | cm/cm/°C |
| TD | ISO11359-22 | 8.3E-05 | cm/cm/°C | |
| RTIElec | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 | °C |
| 3.0mm | UL746 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High arc combustion index (HAI) | 1.6mm | UL746 | PLC1 | |
| 3.0mm | UL746 | PLC1 | ||
| High voltage arc ignition resistance index | PLC | UL746 | PLC6 | |
| Hot wire ignition (HWI) | 1.6mm | UL746 | PLC3 | |
| 3.0mm | UL746 | PLC3 | ||
| Surface resistivity | IEC600932 | 3.8E+14 | ohms | |
| Volume resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Electrical strength | IEC60243-12 | 42 | KV/mm | |
| Relative permittivity | 1MHz | ASTM D1646 | 2.80 | |
| Dissipation factor | 1MHz | ASTM D1646 | 0.010 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC0 | |
| Compared to the leakage trace index | ISO 2577 | 200 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | NoBreak | |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 114 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.