PC/ABS CYCOLOY™ XCY620S-76701 SABIC INNOVATIVE NANSHA
157
- Unit Price:
- $2843 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 91.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility
- Application Areas:Electrical applications Home appliance components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 25.0 | cm3/10min | |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.30 | % |
| Saturation,23°C | ISO62 | 0.40 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.13 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2200 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| Break | ISO527-2/50 | 56.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 4.5 | % |
| Break | ISO527-2/50 | 100 | % | |
| Bending modulus 2 | 50.0mmSpan | ASTMD790 | 2300 | Mpa |
| Bending modulus 3 | ISO178 | 2200 | Mpa | |
| Bending stress 3,4 | ISO178 | 82.0 | Mpa | |
| Flexural Strength2 | Yield,50.0mmSpan | ASTMD790 | 86.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 128 | °C |
| Hot deformation temperature 8 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 108 | °C |
| Hot deformation temperature 8 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 106 | °C |
| Vicat softening temperature | ASTMD15259 | 129 | °C | |
| ISO306/B120 | 130 | °C | ||
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| 100°C10 | IEC60695-10-2 | Pass | ||
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+16 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 39 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CharpyUnnotchedImpactStrength6 | 23°C | ISO179/1eU | NoBreak | |
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 40 | kJ/m² |
| 23°C | ISO180/1A | 55 | kJ/m² | |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 65.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 55.0 | J | |
| Impact strength of simply supported beam gap 5 | -30°C | ISO179/1eA | 45 | kJ/m² |
| 23°C | ISO179/1eA | 60 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.