PC/ABS CYCOLOY™ XCY620-100 SABIC INNOVATIVE NANSHA
142
- Unit Price:
- $3221 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan
- Application Areas:Electrical applications Home appliance components
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 260°C/5.0kg | ASTMD1238 | 22 | g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 18.0 | cm3/10min |
| MeltViscosity | 260°C,1500sec^-1 | ISO11443 | 195 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 3 | Yield | ASTMD638 | 4.7 | % |
| Tensile modulus 2 | ASTMD638 | 2300 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 55.0 | Mpa |
| Break | ASTMD638 | 52.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2300 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 89.0 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 120 | % |
| Bending modulus 5 | ISO178 | 2200 | Mpa | |
| Bending strength 5,6 | ISO178 | 83.0 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2200 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| Break | ISO527-2/50 | 51.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 4.5 | % |
| Break | ISO527-2/50 | 120 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 107 | °C |
| thermal conductivity | ISO8302 | 0.20 | W/m/K | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 11 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 | °C | |
| Vicat softening temperature | ASTMD152512 | 127 | °C | |
| -- | ISO306/B50 | 127 | °C | |
| -- | ISO306/B120 | 129 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 35 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 56.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.