Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	24 hr	ASTM D570	0.10	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.40	%
Melt flow rate	260°C/5.0 kg	ASTM D1238	17	g/10 min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
elongation	Break	ASTM D638	75	%
Bending modulus	50.0 mm Span	ASTM D790	2300	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	84.0	Mpa
Tensile strength	Yield	ASTM D638	54.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature		ASTM D15254	129	°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	123	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	129	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	107	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	110	°C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
thermal conductivity		ASTM C177	0.20	W/m/K
RTI		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI Elec		UL 746	60.0	°C

Electrical performance	Test Method	Test Result
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 2
Hot wire ignition (HWI)	UL 746	PLC 2
High arc combustion index (HAI) 6	UL 746	PLC 0
Arc resistance 5	ASTM D495	PLC 6

injection	Test Result	Unit
drying time	3.0 到 4.0	hr
Suggested injection volume	30 到 80	%
Temperature at the rear of the barrel	250 到 290	°C
Temperature in the middle of the barrel	255 到 295	°C
Temperature at the front of the material cylinder	260 到 300	°C
Spray nozzle temperature	275 到 300	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.038 到 0.076	mm
drying temperature	105 到 110	°C
Suggested maximum moisture content	0.040	%
Processing (melt) temperature	275 到 300	°C
Mold temperature	60 到 90	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	-30°C, Total Energy	ASTM D3763	33.0	J
Dart impact equipped with measuring instruments	Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	40.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Gardner glossiness	60°, 无织构	ASTM D523	30

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.