PC/ABS CYCOLOY™ CX7240-701 SABIC INNOVATIVE NANSHA
216
- Unit Price:
- $5877 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 135MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High impact resistance High mobility
- Application Areas:Electrical field Electronic field Electronic display Engine hood parts Aerospace Applications Nursing supplies Architectural application Outdoor applications Liquid handling Medical supplies Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.20 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.10 | % | |
| Density/specific gravity | ASTMD792 | 1.19 | g/cm³ | |
| ISO1183 | 1.20 | g/cm³ | ||
| Melt mass flow rate | 260°C/2.16kg | ASTMD1238 | 18 | g/10min |
| Melt volume flow rate | 260°C/2.16kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2600 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2600 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 65.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 65.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 58.0 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 50.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 4.1 | % |
| Tensile strain | Yield | ISO527-2/50 | 4.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 100 | % |
| Tensile strain | Break | ISO527-2/50 | 90 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2500 | Mpa |
| Bending modulus 5 | ISO178 | 2500 | Mpa | |
| Bending strength 5,6 | ISO178 | 96.0 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 104 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 100 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 89.0 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 99.0 | °C | |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 93.0 | °C |
| Evolution Calendar intelligent importer | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Vicat softening temperature | ASTMD152512 | 110 | °C | |
| -- | ISO306/B50 | 110 | °C | |
| -- | ISO306/B120 | 113 | °C | |
| BallPressure Test | 75°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| thermal conductivity | ISO8302 | 0.20 | W/m/K | |
| RTIElec | UL746 | 90.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 35 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC3 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C7 | ISO179/1eA | 10 | kJ/m² |
| 23°C8 | ISO179/1eA | 22 | kJ/m² | |
| 23°C7 | ISO179/1eA | 20 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 180 | J/m |
| 23°C | ASTMD256 | 700 | J/m | |
| -30°C9 | ISO180/1A | 10 | kJ/m² | |
| -30°C10 | ISO180/1A | 10 | kJ/m² | |
| 23°C9 | ISO180/1A | 25 | kJ/m² | |
| 23°C10 | ISO180/1A | 20 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 65.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.60mm | UL94 | V-1 | |
| 0.75mm | UL94 | V-0 | ||
| 1.5mm | UL94 | 5VB | ||
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 0.75mm13 | IEC60695-2-12 | 960 | °C |
| 0.75mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.75mm13 | IEC60695-2-13 | 775 | °C |
| 1.0mm | IEC60695-2-13 | 825 | °C | |
| 1.5mm13 | IEC60695-2-13 | 775 | °C | |
| 3.0mm13 | IEC60695-2-13 | 775 | °C | |
| 3.0mm | IEC60695-2-13 | 800 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.