PC/ABS CYCOLOY™ MC1300-100 SABIC INNOVATIVE NANSHA
226
- Unit Price:
- $3115 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 196.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility Easy electroplating
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 260°C/5.0 kg | ASTM D1238 | 14 | g/10 min |
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.50 到 0.80 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 2130 | Mpa | |
| Tensile strength 3 | Yield | ASTM D638 | 50.0 | Mpa |
| Break | ASTM D638 | 44.0 | Mpa | |
| Elongation rate 3 | Yield | ASTM D638 | 8.6 | % |
| Break | ASTM D638 | 150 | % | |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2060 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 72.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 115 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 98.0 | °C | |
| Vicat softening temperature | ASTM D15255 | 111 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 7.2E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.20 | W/m/K |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 100 到 105 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 到 80 | % | ||
| Temperature at the rear of the barrel | 250 到 280 | °C | ||
| Temperature in the middle of the barrel | 255 到 290 | °C | ||
| Temperature at the front of the material cylinder | 255 到 290 | °C | ||
| Spray nozzle temperature | 260 到 290 | °C | ||
| Processing (melt) temperature | 260 到 290 | °C | ||
| Mold temperature | 75 到 100 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C, Total Energy | ASTM D3763 | 33.0 | J |
| 23°C, Total Energy | ASTM D3763 | 40.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.