PC CH8105 1002 B CANGZHOU DAHUA

Unit Price:
$1766 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
15000MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow2.0mm	ISO 294	0.50-0.70	%
Shrinkage rate	Shrinkage rate	垂直2.0mm	ISO 294	0.50-0.70	%
Water absorption rate	23°C24hr	ISO 62	0.32	%
Water absorption rate	Water absorption rate	23℃ 50RH	ISO 62	0.15	%
Melt index	300°C 1.2kg	ISO 1133	10	g/10min
proportion		ISO 1183	1.2	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Impact of simply supported beam gap	23℃	ISO 179	75	kJ/㎡
Cantilever beam gap impact	23℃	ISO 180	70	kJ/㎡
Simple supported beam without notch impact	23℃	ISO 179	NB	kJ/㎡
Cantilever beam without notch impact	23℃	ISO 180	NB	kJ/㎡
Tensile modulus	1.0mm/min	ISO 527	2400	Mpa
tensile strength	Yield50mm/min	ISO 527	60	Mpa
elongation	Yield50mm/min	ISO 527	6	%
elongation	elongation	Break50mm/mi	ISO 527	150	%
Bending modulus	2.0mm/min	ISO 178	2410	Mpa
bending strength	Yield2.0mm/min	ISO 178	97	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	Annealed0.45MPa	ISO 75	144	°C
Hot deformation temperature	Hot deformation temperature	Unannealed1.8MPa	ISO 75	128	°C
Glass transition temperature	10℃/min	ISO 11357	149	°C
Vicat softening temperature	50℃/hr 50N	ISO 306	149	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistance	2.0mm	IEC 60093	10000000000000000	Ω
Anti leakage trace index		IEC 60112	250	V
Insulation strength	1.0mm	IEC 60243	34	KV/mm
Volume resistance	2.0mm	IEC 60093	200000000000000000	Ω.cm
Dissipation factor	100Hz	IEC 60250	0.001
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.01
Dielectric constant	100Hz	IEC 60250	3.1
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness		ISO 2039	120

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ISO 489	1.586
transmissivity		ISO 13468	89	%
Xiudu	2000㎛	ISO 14782	0.8	%

Flame retardant performance	Test Condition	Test Method	Test Result	Unit
Fire rating	1.5mm	UL94	HB
Fire rating	Fire rating	3.0mm	UL94	HB
Relative temperature of heating wire	1.5mm	IEC 60695	875	°C
Relative temperature of heating wire	Relative temperature of heating wire	3mm	IEC 60695	960	°C
Extreme Oxygen Index		ISO 4589	27	%
Ignition temperature of heating wire	1.5mm	IEC 60695	875	°C
Ignition temperature of heating wire	Ignition temperature of heating wire	3mm	IEC 60695	875	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.