PC CH8105 1001 CANGZHOU DAHUA
108
- Unit Price:
- $1751 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 320MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting High impact resistance Low viscosity transparent Demolding performance
- Application Areas:film Electronic and electrical Industrial components Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow2.0mm | ISO 294 | 0.50-0.70 | % |
| 垂直2.0mm | ISO 294 | 0.50-0.70 | % | |
| Water absorption rate | 23°C24hr | ISO 62 | 0.32 | % |
| 23℃ 50RH | ISO 62 | 0.15 | % | |
| Melt index | 300°C 1.2kg | ISO 1133 | 10 | g/10min |
| proportion | ISO 1183 | 1.2 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact of simply supported beam gap | 23℃ | ISO 179 | 75 | kJ/㎡ |
| Cantilever beam gap impact | 23℃ | ISO 180 | 70 | kJ/㎡ |
| Simple supported beam without notch impact | 23℃ | ISO 179 | NB | kJ/㎡ |
| Cantilever beam without notch impact | 23℃ | ISO 180 | NB | kJ/㎡ |
| Tensile modulus | 1.0mm/min | ISO 527 | 2400 | Mpa |
| tensile strength | Yield50mm/min | ISO 527 | 60 | Mpa |
| elongation | Yield50mm/min | ISO 527 | 6 | % |
| Break50mm/mi | ISO 527 | 150 | % | |
| Bending modulus | 2.0mm/min | ISO 178 | 2410 | Mpa |
| bending strength | Yield2.0mm/min | ISO 178 | 97 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | Annealed0.45MPa | ISO 75 | 144 | °C |
| Unannealed1.8MPa | ISO 75 | 128 | °C | |
| Glass transition temperature | 10℃/min | ISO 11357 | 149 | °C |
| Vicat softening temperature | 50℃/hr 50N | ISO 306 | 149 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistance | 2.0mm | IEC 60093 | 10000000000000000 | Ω |
| Anti leakage trace index | IEC 60112 | 250 | V | |
| Insulation strength | 1.0mm | IEC 60243 | 34 | KV/mm |
| Volume resistance | 2.0mm | IEC 60093 | 200000000000000000 | Ω.cm |
| Dissipation factor | 100Hz | IEC 60250 | 0.001 | |
| 1MHz | IEC 60250 | 0.01 | ||
| Dielectric constant | 100Hz | IEC 60250 | 3.1 | |
| 1MHz | IEC 60250 | 3 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ISO 2039 | 120 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.586 | ||
| transmissivity | ISO 13468 | 89 | % | |
| Xiudu | 2000㎛ | ISO 14782 | 0.8 | % |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| Relative temperature of heating wire | 1.5mm | IEC 60695 | 875 | °C |
| 3mm | IEC 60695 | 960 | °C | |
| Extreme Oxygen Index | ISO 4589 | 27 | % | |
| Ignition temperature of heating wire | 1.5mm | IEC 60695 | 875 | °C |
| 3mm | IEC 60695 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.