PC Makrolon® 1695 551022 COVESTRO BELGIUM
127
- Unit Price:
- $5312 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD：2.0 mm Across Flow : 0.0787 in | ISO 294-4 | 0.75 | % |
| Melt mass flow rate | 330℃，2.16kg 330℃/2.16 kg | ISO 1133 | 46 | g/10min |
| Density (73 ° F) | ISO 1183 | 1.18 | g/cm³ | |
| Melt volume flow rate | 330℃，2.16 kg 330℃/2.16 kg | ISO 1133 | 45 | cm3/10min |
| Shrinkage rate | MD：2.0 mm Flow : 0,0787 in | ISO 294-4 | 0.75 | % |
| Water absorption rate | Saturation，23℃ Saturation，23℃ | ISO 62 | 0.3 | % |
| Equilibrium，23℃，50% RH Equilibrium，23℃，50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 68 | Mpa |
| Bending modulus | 23℃ 23℃ 3 | ISO 178 | 2400 | Mpa |
| Bending strength | 23℃ | ISO 178 | 100 | Mpa |
| Ball pressure hardness | ISO 2039-1 | 120 | Mpa | |
| Tensile modulus | 23℃ 23℃ | ISO 527-1-2 | 2400 | Mpa |
| Tensile strain | Yield，23℃ Yield，23℃ | ISO 527-2/50 | 6.2 | % |
| Nominal tensile fracture strain | 23℃ 23℃ | ISO 527-2/50 | > 50 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrolytic corrosion | 23℃ 23℃ | IEC 60426 | A1 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 10000000000000000 | ohms | |
| Volume resistivity | 23℃ 23℃ | IEC 60093 | 100000000000000000 | ohms·cm |
| Dielectric strength | 23 ℃，1 mm 23℃，1.00 mm | IEC 60243-1 | 35 | KV/mm |
| Relative permittivity | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 3 | |
| Relative permittivity | 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 2.9 | |
| Dissipation factor | 23℃，100 Hz 23°C, 100 Hz | IEC 60250 | 0.001 | |
| Dissipation factor | 23℃，1 MHz 23°C, 1 MHz | IEC 60250 | 0.009 | |
| Compared to the leakage trace index | Solution A Solution A | IEC 60112 | 250 | V |
| Solution B Solution B | IEC 60112 | 125 | V | |
| Flame retardant grade | 1.50 mm 1.5 mm | UL 94 | HB | |
| Flame retardant grade | 3.00 mm 3.0 mm | UL 94 | HB | |
| Flammability index of heating wire | 2.0 mm 2.0 mm | IEC 60695-2-12 | 900 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 26 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | |||
| -30℃ -30°C | ISO 179/1eU | No Break | ||
| 23℃ 23°C | ISO 179/1eU | No Break |
| Optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.578 | ||
| Light transmittance | 1000 µm 1000 µm | ISO 13468-2 | 89 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23~55℃ TD：23 to 55℃ | ISO 11359-2 | 0.000065 | 1/℃ |
| Linear coefficient of thermal expansion | MD：23~55℃ MD：23 to 55℃ | ISO 11359-2 | 0.000065 | 1/℃ |
| Relative temperature index | 电气性能 电气性能 | UL 746 | 140 | °C |
| 冲击机械性能 冲击机械性能 | UL 746 | 130 | °C | |
| Relative temperature index | 强度机械性能 强度机械性能 | UL 746 | 140 | °C |
| Vicat softening temperature | B120 B120 | ISO 306/B120 | 158 | °C |
| Hot deformation temperature | 1.8 MPa，Unannealed 1.8 MPa，Unannealed | ISO 75-2/A | 138 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.