PC EXL1414T-NA8A005T SABIC INNOVATIVE NANSHA
115
- Unit Price:
- $4744 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 73MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.40到0.80 | % |
| TD:3.20mm | 内部方法 | 0.40到0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.12 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.093 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.50 | cm3/10min |
| Density/specific gravity | ASTMD792,ISO1183 | 1.19 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | --6,7 | ISO178 | 88.6 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 92.0 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 57.6 | Mpa |
| Yield | ISO527-2/50 | 56.8 | Mpa | |
| Break4 | ASTMD638 | 59.1 | Mpa | |
| Break | ISO527-2/50 | 55.3 | Mpa | |
| Tensile modulus | --3 | ASTMD638 | 2190 | Mpa |
| -- | ISO527-2/1 | 2310 | Mpa | |
| elongation | Yield4 | ASTMD638 | 5.6 | % |
| Yield | ISO527-2/50 | 5.4 | % | |
| Break4 | ASTMD638 | 120 | % | |
| Break | ISO527-2/50 | 110 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2180 | Mpa |
| --6 | ISO178 | 2120 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 121 | °C |
| 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 116 | °C | |
| RTIElec | UL746 | 130 | °C | |
| Linear coefficient of thermal expansion | MD:23to80°C | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| TD:-40to95°C | ASTME831 | 8E-05 | cm/cm/°C | |
| TD:23to80°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| MD:-40to95°C | ASTME831 | 6.7E-05 | cm/cm/°C | |
| RTI | UL746 | 130 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | 通过 | |
| Vicat softening temperature | -- | ASTMD152511,ISO306/B12011 | 139 | °C |
| -- | ISO306/B50 | 138 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 77.4 | J |
| 23°C,TotalEnergy | ASTMD3763 | 75.5 | J | |
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 60 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | 无断裂 | |
| 23°C | ISO180/1U | 无断裂 | ||
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 710 | J/m |
| 23°C | ASTMD256 | 820 | J/m | |
| -30°C9 | ISO180/1A | 55 | kJ/m² | |
| 23°C9 | ISO180/1A | 65 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L-Sale | ISO2039-2 | 87 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 2540µm | ASTMD1003 | 3.0 | % |
| transmissivity | 2540µm | ASTMD1003 | 82.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 3.0mm | UL94 | V-2 | ||
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 0.8mm | IEC60695-2-13 | 850 | °C |
| 3.0mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.