Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Water absorption rate | Equilibrium,23°C | ASTMD570 | 0.35 | % |
| Water absorption rate | Equilibrium,100°C | ASTMD570 | 0.58 | % |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 15 | g/10min |
| Specific volume | | ASTMD792 | 0.835 | cm³/g |
| Outdoor applicability | | UL746C | f1 | |
| Outdoor applicability | | UL746C | f1 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile strength 2 | Yield | ASTMD638 | 62.1 | Mpa |
| Tensile strength 2 | Break | ASTMD638 | 55.8 | Mpa |
| Elongation rate 2 | Yield | ASTMD638 | 7.0 | % |
| Elongation rate 2 | Break | ASTMD638 | 90 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2240 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 91.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| thermal conductivity | | ASTMC177 | 0.19 | W/m/K |
| thermal conductivity | | ASTMC177 | 0.19 | W/m/K |
| RTIElec | | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | | UL746 | 120 | °C |
| RTIStr | | UL746 | 130 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
| Vicat softening temperature | | ASTMD15255 | 152 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot wire ignition | HWI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC2 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Dielectric constant | 1MHz | ASTMD150 | 2.96 | |
| Dielectric constant | 50Hz | ASTMD150 | 3.01 | |
| Dielectric constant | 60Hz | ASTMD150 | 3.01 | |
| Volume resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Volume resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 60Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 1MHz | ASTMD150 | 0.010 | |
| Arc resistance 6 | | ASTMD495 | PLC7 | |
| Arc resistance 6 | | ASTMD495 | PLC7 | |
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 17 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Tensile impact strength 4 | | ASTMD1822 | 525 | kJ/m² |
| Tensile impact strength 4 | | ASTMD1822 | 525 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ASTMD785 | 70 | |
| Rockwell hardness | R-Sale | ASTMD785 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| transmissivity | 2540µm | ASTMD1003 | 85.0 | % |
| Refractive index | | ASTMD542 | 1.586 | |
| Refractive index | | ASTMD542 | 1.586 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.0mm | UL94 | V-0 | |
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.