PC LEXAN™ EXL9414-BK1A068 SABIC INNOVATIVE NANSHA

134

Unit Price:
$4494 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
36MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility High ductility at low tem
Application Areas:Electronic display Quick charging phone case
Color:--
Grade:Cold resistant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	300°C/1.2 kg	ASTM D1238	12	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Shrinkage rate	Flow : 3.20 mm	内部方法	0.40 到 0.80	%
Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.40 到 0.80	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 2	ASTM D638	2110	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2140	Mpa
elongation	Yield 3	ASTM D638	5.8	%
	elongation	Yield	ISO 527-2/50	5.6	%
		elongation	Break 3	ASTM D638	110	%
		elongation	elongation	Break	ISO 527-2/50	110	%
Bending modulus	50.0 mm Span 4	ASTM D790	2190	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2180	Mpa
Tensile strength	Yield 3	ASTM D638	56.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	57.0	Mpa
		Tensile strength	Break 3	ASTM D638	62.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	60.0	Mpa
Bending stress	-- 5, 6	ISO 178	86.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	88.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ISO 306/B50	136	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	138	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.9E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.4E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.3E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5	cm/cm/°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	134	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	131	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	118	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	117	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	1.10 GHz	ASTM ES7-83	6.0E-3
Surface resistivity		ASTM D257	> 1.0E+16	ohms
Dielectric constant	1.10 GHz	ASTM ES7-83	2.78
Volume resistivity		ASTM D257	> 1.0E+16	ohms·cm
Dielectric strength	3.20 mm, in Oil	ASTM D149	13	KV/mm

injection	Test Result	Unit
drying temperature	120	°C
Suggested maximum moisture content	0.020	%
Processing (melt) temperature	295 到 315	°C
Mold temperature	70 到 95	°C
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	270 到 295	°C
Temperature in the middle of the barrel	280 到 305	°C
Temperature at the front of the material cylinder	295 到 315	°C
Spray nozzle temperature	290 到 310	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	67.0	J
Impact strength of simply supported beam gap 7	-30°C	ISO 179/1eA	29	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C	ISO 179/1eA	75	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	L -Sale	ASTM D785	83
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	117

flammability	Test Condition	Test Method	Test Result	Unit
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	39	%
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	850	°C
UL flame retardant rating	0.50 mm	UL 94	V-2
	UL flame retardant rating	0.8 mm	UL 94	V-1
		UL flame retardant rating	1.0 mm	UL 94	V-0
			UL flame retardant rating	1.5 mm	UL 94	5VB
			UL flame retardant rating	UL flame retardant rating	3.1 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.