PC LNP™ THERMOCOMP™ D151-701 SABIC INNOVATIVE NANSHA
122
- Unit Price:
- $6347 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Non chloro non bromine fl
- Application Areas:Electronic and Electrical Electronic display
- Color:--
- Grade:Flame retardant enhanced grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 14 | g/10min |
| 300°C/2.16kg | ASTMD1238 | 29 | g/10min | |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 13.0 | cm3/10min |
| 300°C/2.16kg | ISO1133 | 27.0 | cm3/10min | |
| Shrinkage rate | MD:24hr | ASTMD955 | 0.30到0.50 | % |
| TD:24hr | ASTMD955 | 0.30到0.50 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.080 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --1 | ASTMD638 | 4400 | Mpa | |
| Fracture 2 | ASTMD638 | 83.0 | Mpa | |
| crack | ISO527-2/5 | 82.0 | Mpa | |
| Fracture 3 | ASTMD638 | 3.6 | % | |
| crack | ISO527-2/5 | 3.6 | % | |
| 50.0mm span 4 | ASTMD790 | 4070 | Mpa | |
| --5 | ISO178 | 4010 | Mpa | |
| --6 | ISO178 | 133 | Mpa | |
| Fracture, 50.0mm span 7 | ASTMD790 | 131 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 121 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 117 | °C | |
| Linear coefficient of thermal expansion | MD:23to80°C | ISO11359-2 | 3.4E-05 | cm/cm/°C |
| TD:23to80°C | ISO11359-2 | 7.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1.10GHz | 内部方法 | 3.07 | |
| 1.90GHz | 内部方法 | 3.06 | ||
| 5.00GHz | 内部方法 | 3.06 | ||
| 10.0GHz | 内部方法 | 3.05 | ||
| Dissipation factor | 1.10GHz | 内部方法 | 6.7E-03 | |
| 1.90GHz | 内部方法 | 6.5E-03 | ||
| 5.00GHz | 内部方法 | 6.9E-03 | ||
| 10.0GHz | 内部方法 | 6.9E-03 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 8 | 23°C | ISO179/1eA | 13 | kJ/m² |
| Simply supported beam without notch impact strength 9 | 23°C | ISO179/1eU | 50 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 710 | J/m |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 22.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.300mm | UL94 | V-2 | |
| 0.400mm | UL94 | V-1 | ||
| 0.600mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.