PC Makrolon® 6487 901510 COVESTRO SHANGHAI
155
- Unit Price:
- $3099 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 105.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Good demolding performanc Medium viscosity Flame retardant High impact resistance UV curing Processability
- Application Areas:Electrical field Electronic field Household appliances Household appliances Architectural application Automotive sector Barrel disposable Medical Supplies
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density 2 | ISO60 | 0.64 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.60to0.80 | % |
| MD | ISO2577 | 0.60to0.80 | % | |
| TD:2.00mm3 | ISO294-4 | 0.75 | % | |
| MD:2.00mm3 | ISO294-4 | 0.70 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2450 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending modulus 4 | 23°C | ISO178 | 2450 | Mpa |
| Bending stress 4 | 3.5%Strain,23°C | ISO178 | 75.0 | Mpa |
| 23°C | ISO178 | 99.0 | Mpa | |
| Bending strain 5 | 23°C | ISO178 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 134 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 122 | °C | |
| Glass transition temperature 8 | ISO11357-2 | 141 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 141 | °C | |
| BallPressure Test | 135°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 8E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 225 | V |
| SolutionB | IEC60112 | 125 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 55.0 | J |
| 23°C | ISO6603-2 | 50.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6000 | N |
| 23°C | ISO6603-2 | 5200 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 117 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 | °C |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 900 | °C |
| 3.0mm | IEC60695-2-13 | 930 | °C | |
| Extreme Oxygen Index 10 | ISO4589-2 | 36 | % | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut | ISO7391-PC,MFLR,(,,)-09-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.