PC LNP™ THERMOCOMP™ DX11355-BKNAT SABIC INNOVATIVE NANSHA
135
- Unit Price:
- $8858 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 98MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High mobility
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 12 | g/10 min |
| Shrinkage rate | Flow : 24hr | 0.5 | % | |
| Across Flow : 24hr | 0.5 | % | ||
| Water absorption rate | 24 hr, 23°C, 50% RH | ASTM D570 | 0.01 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 2600 | Mpa | |
| Tensile strength 3 | Yield | 58 | Mpa | |
| Break | 52 | Mpa | ||
| Elongation rate 3 | Yield | 5.4 | % | |
| Break | 70 | % | ||
| Bending modulus 4 | 50.0 mm Span | ASTM D790 | 2400 | Mpa |
| Bending strength 4 | Yield, 50.0 mm Span | 90 | Mpa | |
| Break, 50.0 mm Span | 89 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature under load (1.8 MPa, unannealed), 3.20 mm) | ASTM D648 | 114 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | 0.000062 | cm/cm/°C | |
| 垂直 : -40 to 40°C | 0.000067 | cm/cm/°C | ||
| RTI Elec | UL 746B | 80 | °C | |
| RTI Imp | UL 746B | 80 | °C | |
| RTI | UL 746B | 80 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 1.00 GHz | IEC 60250 | 2.92 | |
| Dissipation factor | 1.00 GHz | IEC 60250 | 0.007 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 100 到 110 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.02 | % | ||
| Suggested injection volume | 30 到 80 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 250 到 290 | °C | ||
| Temperature in the middle of the barrel | 255 到 295 | °C | ||
| Temperature at the front of the material cylinder | 260 到 300 | °C | ||
| Spray nozzle temperature | 275 到 300 | °C | ||
| Processing (melt) temperature | 275 到 300 | °C | ||
| Mold temperature | 60 到 90 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.038 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact (-30 ° C) | ASTM D4812 | 2100 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | > 0.60 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.