PC Makrolon® 3208 550111 COVESTRO BELGIUM
142
- Unit Price:
- $6592 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance high molecular weight Drinking water contact
- Application Areas:building materials Transportation equipment Lighting fixtures
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density (73 ° F) | ISO 1183 | 1.2 | g/cm³ | |
| Apparent Density 2 2 | ISO 60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300℃，1.20kg 300℃/1.2 kg | ISO 1133 | 5.5 | g/10min |
| Melt volume flow rate | 300℃，1.2 kg 300℃/1.2 kg | ISO 1133 | 5 | cm3/10min |
| Shrinkage rate | TD Across Flow | ISO 2577 | 0.60 to 0.80 | % |
| Shrinkage rate | MD Flow | ISO 2577 | 0.60 to 0.80 | % |
| TD：2.0 mm Across Flow : 0.0787 in 3 3 | ISO 294-4 | 0.75 | % | |
| Shrinkage rate | MD：2.0 mm Flow : 0.0787 in 3 3 | ISO 294-4 | 0.7 | % |
| Water absorption rate | Saturation，23℃ Saturation，23℃ | ISO 62 | 0.3 | % |
| Water absorption rate | Equilibrium，23℃，50% RH Equilibrium，23℃，50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23℃ | ISO 527-1-2 | 2350 | Mpa |
| Tensile strength | Break，23℃ | ISO 527-2/50 | 75 | Mpa |
| Yield，23℃ | ISO 527-2/50 | 65 | Mpa | |
| Tensile strain | Break，23℃ | ISO 527-2/50 | 120 | % |
| Yield，23℃ | ISO 527-2/50 | 6.3 | % | |
| Nominal tensile fracture strain | 23℃ | ISO 527-2/50 | > 50 | % |
| Tensile Creep Modulus（1 hr） Tensile Creep Modulus (1 hr) | ISO 899-1 | 2200 | Mpa | |
| Tensile creep modulus | 1000 hr | ISO 899-1 | 1900 | Mpa |
| Bending modulus Bending modulus 4 | 23℃ 23℃ 4 | ISO 178 | 2350 | Mpa |
| Flexural Stress 4 4 | 3.50% Strain，23℃ 3.5% Strain, 23°C | ISO 178 | 72 | Mpa |
| Flexural Stress 4 5 | 23℃ 23°C | ISO 178 | 95 | Mpa |
| 弯曲应变 Flexural Strain at Flexural Strength 5 (23°C) 5 | ISO 178 | 7.2 | % | |
| Ball pressure hardness | ISO 2039-1 | 111 | Mpa |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | -30℃，Complete Break -22°F, Complete Break | ISO 7391 | 18 | kJ/m² |
| 23℃，Partial Break 73°F, Partial Break | ISO 7391 | 80 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60℃ -60°C | ISO 179/1eU | No Break | |
| -30℃ -30°C | ISO 179/1eU | No Break | ||
| 23℃ 23°C | ISO 179/1eU | No Break | ||
| Impact strength of cantilever beam gap | -30℃，Complete Break -22°F, Complete Break | ISO 7391 | 20 | kJ/m² |
| 23℃，Partial Break 73°F, Partial Break | ISO 7391 | 75 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30℃ -30°C | ISO 6603-2 | 75 | J |
| 23℃ 23°C | ISO 6603-2 | 65 | J | |
| Multi axis Instrumented Peak Impact Force | -30℃ -30°C | ISO 6603-2 | 6700 | N |
| 23℃ 23°C | ISO 6603-2 | 5800 | N |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flash Ignition Temperature Flash Ignition Temperature | ASTM D1929 | 480 | °C | |
| Spontaneous combustion temperature | ASTM D1929 | 550 | °C |
| Optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.587 | ||
| Light transmittance | 1000 µm | ISO 13468-2 | 89 | % |
| 2000 µm | ISO 13468-2 | 89 | % | |
| Light transmittance | 3000 µm | ISO 13468-2 | 88 | % |
| 4000 µm | ISO 13468-2 | 87 | % | |
| Haze | 3000 µm | ISO 14782 | < 0.80 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass transition temperature | ISO 11357-2 | 150 | °C | |
| Vicat softening temperature | B50 -- | ISO 306 | 150 | °C |
| B120 -- | ISO 306/B120 | 151 | °C | |
| Ball pressure test | 141℃ 141℃ | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | TD：23~55℃ | ISO 11359-2 | 0.000065 | 1/℃ |
| MD：23~55℃ | ISO 11359-2 | 0.000065 | 1/℃ | |
| Thermal conductivity coefficient | 23℃ 23℃ 9 | ISO 8302 | 0.2 | W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.