Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electronic display Lighting applications
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	300°C/1.2 kg	ASTM D1238	10	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00	cm3/10min
Shrinkage rate	Flow : 3.20 mm	内部方法	0.55 到 0.75	%
Shrinkage rate	Shrinkage rate	Across Flow : 3.20 mm	内部方法	0.60 到 0.80	%
Water absorption rate	Saturation, 23°C	ISO 62	0.13	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.10	%
Outdoor applicability		UL 746C	f1

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 2	ASTM D638	2520	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350	Mpa
Tensile strength	Yield 3	ASTM D638	67.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	66.0	Mpa
		Tensile strength	Break 3	ASTM D638	55.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	53.0	Mpa
elongation	Yield 3	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break 3	ASTM D638	55	%
		elongation	elongation	Break	ISO 527-2/50	56	%
Bending modulus	50.0 mm Span 4	ASTM D790	2450	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2450	Mpa
Bending stress	-- 5, 6	ISO 178	101	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	107	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	131	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Ae	120	°C
Vicat softening temperature	--	ASTM D152510	136	°C
	Vicat softening temperature	--	ISO 306/B50	137	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	139	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.7E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.7E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.9E-5	cm/cm/°C
RTI Elec		UL 746	125	°C
RTI Imp		UL 746	120	°C
RTI		UL 746	125	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric constant	1.10 GHz	ASTM ES7-83	2.79
Dissipation factor	1.10 GHz	ASTM ES7-83	5.7E-3

injection	Test Result	Unit
drying temperature	120	°C
drying time	3.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	260 到 280	°C
Temperature in the middle of the barrel	270 到 295	°C
Temperature at the front of the material cylinder	280 到 305	°C
Spray nozzle temperature	275 到 300	°C
Processing (melt) temperature	280 到 305	°C
Mold temperature	70 到 95	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 7	-30°C	ISO 179/1eA	7.0	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C	ISO 179/1eA	10	kJ/m²
The impact strength of a simply supported beam without a notch is 7	-30°C	ISO 179/1eU	无断裂
	The impact strength of a simply supported beam without a notch is 7	23°C	ISO 179/1eU	无断裂
Non notched cantilever beam impact	-30°C	ASTM D4812, ISO 180/1U	无断裂
Non notched cantilever beam impact	Non notched cantilever beam impact	23°C	ASTM D4812, ISO 180/1U	无断裂
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	64.0	J

optical performance	Test Condition	Test Method	Test Result	Unit
transmissivity	2540 µm	ASTM D1003	> 91.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	1.0 mm	UL 94	V-1
		UL flame retardant rating	1.2 mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.2 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.2 mm	IEC 60695-2-13	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.