Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Thermal stability enhance High temperature resistan high viscosity
Application Areas:Electrical field Electronic field Connector Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity	23°C	ISO1183	1.15	g/cm³
Melt mass flow rate	330°C/2.16kg	ISO1133	10	g/10min
Melt volume flow rate	330°C/2.16kg	ISO1133	10.0	cm3/10min
Shrinkage rate 2	TD:2.00mm	ISO294-4	0.85	%
Shrinkage rate 2	Shrinkage rate 2	MD:2.00mm	ISO294-4	0.85	%
Water absorption rate	Saturation,23°C	ISO62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.12	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2/1	2400	Mpa
Tensile stress	Yield,23°C	ISO527-2/50	72.0	Mpa
Tensile strain	Yield,23°C	ISO527-2/50	6.8	%
Nominal tensile fracture strain	23°C	ISO527-2/50	>50	%
Bending modulus 3	23°C	ISO178	2400	Mpa
Bending strength 3	23°C	ISO178	108	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	174	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	159	°C
Vicat softening temperature		ISO306/B120	184	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
RTIElec		UL746	150	°C
Evolution Calendar intelligent importer		UL746	130	°C
RTIStr		UL746	150	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+17	ohms·cm
Dielectric strength	23°C,1.00mm	IEC60243-1	35	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	2.90
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	2.80
Dissipation factor	23°C,100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	8E-03
Leakage Trace Index	SolutionA	IEC60112	450	V
Leakage Trace Index	Leakage Trace Index	SolutionB	IEC60112	100	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	121	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index 5		ISO489	1.573
transmissivity	1000µm	ISO13468-2	89.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB
Burning wire flammability index		IEC60695-2-12	850	°C
Extreme Oxygen Index 4		ISO4589-2	25	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion	23°C	IEC60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.