PC LEXAN™ ML7694-739 SABIC INNOVATIVE NANSHA
102
- Unit Price:
- $2791 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Middle flow Fatigue resistance Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Electronic and electrical Home appliance products
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20到0.40 | % |
| Water absorption rate | Equilibrium,23°C | ASTMD570 | 0.31 | % |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 7.5 | g/10min |
| Specific volume | ASTMD792 | 0.800 | cm³/g | |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength 1 | Break | ASTMD638 | 53.0 | Mpa |
| Bending modulus 3 | 50.0mmSpan | ASTMD790 | 3440 | Mpa |
| Elongation rate 2 | Break | ASTMD638 | 15 | % |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| thermal conductivity | ASTMC177 | 0.20 | W/m/K | |
| RTI | UL746 | 125 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 146 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 142 | °C | |
| RTIElec | UL746 | 120 | °C | |
| Evolution Calendar intelligent importer | UL746 | 110 | °C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 3.2E-05 | cm/cm/°C |
| Vicat softening temperature | ASTMD15257 | 154 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC1 | |
| High arc combustion index | HAI | UL746 | PLC1 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Arc resistance 8 | ASTMD495 | PLC7 | ||
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 18 | KV/mm |
| Volume resistivity | ASTMD257 | >1.0E+17 | ohms·cm | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 2100 | J/m |
| -30°C5 | ISO180/1A | 9.0 | kJ/m² | |
| 23°C6 | ISO180/1A | 10 | kJ/m² | |
| 23°C | ASTMD256 | 100 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.52mm | UL94 | V-0 | |
| 2.99mm | UL94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.