PC LUX9612G-WH8A490X SABIC INNOVATIVE NANSHA

129

Unit Price:
$4838 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Lighting applications
Color:--
Grade:Light diffusion level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.20mm	内部方法	0.50到0.70	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	内部方法	0.60to0.80	%
Water absorption rate	Saturation,23°C	ISO62	0.35	%
	Water absorption rate	Equilibrium,100°C	ASTMD570	0.58	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.15	%
Melt mass flow rate	300°C/1.2kg	ASTMD1238	7.0	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	7.00	cm3/10min
Outdoor applicability		UL746C	f2

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress 2,3		ISO178	94.0	Mpa
Elongation rate 4	Break	ASTMD638	80	%
Bending modulus 5		ISO178	2250	Mpa
Bending strength 6,7		ISO178	95.0	Mpa
Elongation rate 3	Yield	ASTMD638	6.0	%
Tensile modulus 2		ASTMD638	2300	Mpa
Tensile strength 3	Yield	ASTMD638	62.0	Mpa
Tensile strength 3	Tensile strength 3	Break	ASTMD638	65.0	Mpa
Bending modulus 4	50.0mmSpan	ASTMD790	2160	Mpa
Bending strength 4	Yield,50.0mmSpan	ASTMD790	95.0	Mpa
Bending modulus 2		ISO178	2250	Mpa
Tensile modulus		ISO527-2/1	2300	Mpa
Tensile modulus	Tensile modulus		ISO527-2/1	2230	Mpa
Tensile stress	Yield	ISO527-2/50	63.0	Mpa
	Tensile stress	Break	ISO527-2/50	65.0	Mpa
		Tensile stress	Yield	ISO527-2/50	62.0	Mpa
		Tensile stress	Tensile stress	Break	ISO527-2/50	58.0	Mpa
Tensile strain	Break	ISO527-2/50	75	%
	Tensile strain	Yield	ISO527-2/50	6.0	%
	Tensile strain	Tensile strain	Break	ISO527-2/50	100	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
RTIElec		UL746	125	°C
Evolution Calendar intelligent importer		UL746	115	°C
RTIStr		UL746	125	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTMD648	123	°C
Vicat softening temperature		ASTMD152510	140	°C
	Vicat softening temperature	--	ISO306/B50	141	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	142	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05	cm/cm/°C
specific heat		ASTMC351	1260	J/kg/°C
thermal conductivity		ASTMC177	0.20	W/m/K
RTI		UL746	125	°C
BallPressure Test	125°C	IEC60695-10-2	通过
BallPressure Test	BallPressure Test	125°C	IEC60695-10-2	Pass
Hot deformation temperature 6	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	135	°C
Hot deformation temperature 6	Hot deformation temperature 6	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	123	°C
Hot deformation temperature 9	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	135	°C
Hot deformation temperature 9	Hot deformation temperature 9	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	123	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot wire ignition	HWI	UL746	PLC3
High arc combustion index	HAI	UL746	PLC1
Compared to the anti leakage trace index	CTI	UL746	PLC3
Dielectric strength	3.20mm,inAir	ASTMD149	15	KV/mm
Dielectric constant	50Hz	ASTMD150	3.17
	Dielectric constant	60Hz	ASTMD150	3.17
	Dielectric constant	Dielectric constant	1MHz	ASTMD150	2.96
Volume resistivity		IEC60093	>1.0E+15	ohms·cm
Dissipation factor	50Hz	ASTMD150	9E-04
	Dissipation factor	60Hz	ASTMD150	9E-04
	Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.010

Impact performance	Test Condition	Test Method	Test Result	Unit
Cantilever beam without notch impact strength	23°C	ASTMD4812,ISO180/1U	无断裂
Cantilever beam without notch impact strength	Cantilever beam without notch impact strength	-30°C5	ISO180/1U	无断裂
Multi axis Instrumented Impact Energy		ISO6603-2	130	J
Dart impact equipped with measuring instruments	23°C,TotalEnergy	ASTMD3763	70.0	J
Simple supported beam without notch impact strength 4	-30°C	ISO179/1eU	无断裂
Simple supported beam without notch impact strength 4	Simple supported beam without notch impact strength 4	23°C	ISO179/1eU	无断裂
NotchedIzodImpactStrength8	23°C	ISO180/1A	40	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ISO489	1.586

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.30mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	V-0
Burning wire flammability index	0.8mm	IEC60695-2-12	750	°C
	Burning wire flammability index	1.0mm	IEC60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	1.5mm	IEC60695-2-12	850	°C
Hot filament ignition temperature	1.0mm	IEC60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	1.5mm	IEC60695-2-13	850	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.