PC LEXAN™ EXL4419 WH9D245NS SABIC INNOVATIVE NANSHA
108
- Unit Price:
- $4002 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 64MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced Low temperature resistanc
- Application Areas:Electrical field Electrical appliances Electronic field Automotive sector Automotive interior parts Automotive External Parts
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.12 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.46 | % | |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 11 | g/10 min |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 10.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.20 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | -- 5, 6 | ISO 178 | 90.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 95.0 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 53.0 | Mpa |
| Yield | ISO 527-2/5 | 55.0 | Mpa | |
| Break 3 | ASTM D638 | 44.0 | Mpa | |
| Break | ISO 527-2/5 | 43.0 | Mpa | |
| Tensile modulus | -- 2 | ASTM D638 | 3300 | Mpa |
| -- | ISO 527-2/1 | 3300 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 4.5 | % |
| Yield | ISO 527-2/5 | 4.5 | % | |
| Break 3 | ASTM D638 | 20 | % | |
| Break | ISO 527-2/5 | 13 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 3200 | Mpa |
| -- 5 | ISO 178 | 3300 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | -- | ASTM D152510 | 145 | °C |
| -- | ISO 306/B50 | 144 | °C | |
| -- | ISO 306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 4.1E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.9E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 135 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 134 | °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1 MHz | ASTM D150 | 8.6E-3 | |
| 1.90 GHz | 内部方法 | 5.7E-3 | ||
| Surface resistivity | ASTM D257 | 2.9E+17 | ohms | |
| Dielectric constant | 1 MHz | ASTM D150 | 3.04 | |
| 1.90 GHz | 内部方法 | 2.95 | ||
| Volume resistivity | ASTM D257 | 1.8E+17 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 32 | KV/mm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 310 到 330 | °C | ||
| Mold temperature | 80 到 115 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 290 到 310 | °C | ||
| Temperature in the middle of the barrel | 300 到 320 | °C | ||
| Temperature at the front of the material cylinder | 310 到 330 | °C | ||
| Spray nozzle temperature | 305 到 325 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 40.0 | J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 15 | kJ/m² |
| 23°C | ISO 179/1eA | 25 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.