PC Makrolon® 9125C 700051 COVESTRO SHANGHAI

140

Unit Price:
$3568 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Medium viscosity Flame retardant Good demolding performanc Filler: Glass fiber reinf 20% filler by weight 20% filler by weight
Application Areas:--
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD:2.00mm3	ISO294-4	0.35	%
	Shrinkage rate	TD:2.00mm3	ISO294-4	0.45	%
		Shrinkage rate	MD	ISO2577	0.30to0.50	%
		Shrinkage rate	Shrinkage rate	TD	ISO2577	0.30to0.50	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO62	0.10	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO62	0.24	%
Melt mass flow rate	300°C/1.2kg	ISO1133	10	g/10min
Melt volume flow rate	300°C/1.2kg	ISO1133	8.00	cm3/10min
Density/specific gravity	23°C	ISO1183	1.34	g/cm³
Apparent density 2		ISO60	0.64	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending strain 5	23°C	ISO178	3.0	%
TensileCreepModule	1hr	ISO899-1	5700	Mpa
Bending stress 4	23°C	ISO178	140	Mpa
Bending modulus 4	23°C	ISO178	5600	Mpa
Tensile stress	Break,23°C	ISO527-2/5	85.0	Mpa
Tensile strain	Break,23°C	ISO527-2/5	2.5	%
Tensile creep modulus	1000hr	ISO899-1	5200	Mpa
Tensile modulus	23°C	ISO527-2/1	5800	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	142	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	138	°C
RTIElec	1.5mm	UL746	130	°C
Evolution Calendar intelligent importer	1.5mm	UL746	125	°C
RTIStr	1.5mm	UL746	125	°C
Vicat softening temperature	--	ISO306/B50	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/B120	146	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO11359-2	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Thermal conductivity coefficient 8	23°C	ISO8302	0.23	W/m/K
BallPressure Test	136°C	IEC60695-10-2	Pass

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength	23°C,1.00mm	IEC60243-1	36	KV/mm
Relative permittivity	23°C,100Hz	IEC60250	3.30
Relative permittivity	Relative permittivity	23°C,1MHz	IEC60250	3.30
Leakage Trace Index	SolutionA	IEC60112	175	V
Leakage Trace Index	Leakage Trace Index	SolutionB	IEC60112	125	V
Dissipation factor	23°C,100Hz	IEC60250	1E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC60250	9E-03
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C,Complete Break	ISO179/1eU	45	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Complete Break	ISO179/1eU	40	kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO6603-2	5.00	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C	ISO6603-2	5.00	J
CharpyNotchedImpactStrength6	23°C,CompleteBreak	ISO7391	8.0	kJ/m²
NotchedIzodImpactStrength7	23°C,CompleteBreak	ISO7391	8.0	kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO6603-2	800	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23°C	ISO6603-2	800	N

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	148	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.36mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	1.5mm	UL94	V-0
Burning wire flammability index	1.5mm	IEC60695-2-12	960	°C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	960	°C
Extreme Oxygen Index 9		ISO4589-2	35	%
Hot filament ignition temperature	1.5mm	IEC60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	850	°C
Burning rate - US-FMVSS	>1.00mm	ISO3795	passed
FlashIgnitionTemperature		ASTMD1929	470	°C
Needle flame test	MethodK:3.00mm	IEC60695-11-5	2.0	min
	Needle flame test	MethodK:2.00mm	IEC60695-11-5	2.0	min
		Needle flame test	MethodK:1.50mm	IEC60695-11-5	1.0	min
			Needle flame test	MethodF:3.00mm	IEC60695-11-5	2.0	min
				Needle flame test	MethodF:2.00mm	IEC60695-11-5	2.0	min
				Needle flame test	Needle flame test	MethodF:1.50mm	IEC60695-11-5	2.0	min
SelfIgnition		ASTMD1929	550	°C
ApplicationofFlamefromSmallBurner	2.00mm	DIN4102	B2
ApplicationofFlamefromSmallBurner	ApplicationofFlamefromSmallBurner	MethodKandF:2.00mm	DIN53438-1,-3	K1,F1

Supplementary Information	Test Condition	Test Method	Test Result	Unit
ISO Shortcut			ISO7391-PC,MFR,(,,)-09-3,GF20
ElectrolyticalCorrosion	23°C	IEC60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.