PC LEXAN™ HFD4412 BK1E707 SABIC INNOVATIVE NANSHA
89
- Unit Price:
- $3187 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 40MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Electronic display Architectural Application
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 15 | g/10 min |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 14.0 | cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.10 到 0.30 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.10 到 0.30 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 6400 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 96.0 | Mpa |
| Yield | ISO 527-2/5 | 110 | Mpa | |
| Break 3 | ASTM D638 | 96.0 | Mpa | |
| Break | ISO 527-2/5 | 110 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 3.0 | % |
| Yield | ISO 527-2/5 | 2.8 | % | |
| Break | ISO 527-2/5 | 2.7 | % | |
| Bending modulus | 50.0 mm Span | ASTM D790 | 5850 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 159 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 130 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 125 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 7 | ISO 75-2/Af | 127 | °C | |
| Vicat softening temperature | ISO 306/B120 | 143 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 3.0E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI | UL 746 | 80.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 265 到 290 | °C | ||
| Temperature in the middle of the barrel | 275 到 300 | °C | ||
| Temperature at the front of the material cylinder | 290 到 310 | °C | ||
| Spray nozzle temperature | 280 到 305 | °C | ||
| Processing (melt) temperature | 290 到 310 | °C | ||
| Mold temperature | 70 到 95 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 5 | -30°C | ISO 179/1eA | 8.0 | kJ/m² |
| 23°C | ISO 179/1eA | 8.0 | kJ/m² | |
| Simply supported beam without notch impact strength 5 | -30°C | ISO 179/1eU | 48 | kJ/m² |
| 23°C | ISO 179/1eU | 43 | kJ/m² | |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 830 | J/m |
| -30°C 6 | ISO 180/1U | 40 | kJ/m² | |
| 23°C 6 | ISO 180/1U | 42 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 21.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.30 mm | UL 94 | HB | |
| Burning wire flammability index | 2.0 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0 mm | IEC 60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.