PC LEXAN™ HFD1810 NA9E108T SABIC INNOVATIVE NANSHA

125

Unit Price:
$4518 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High mobility copolymer
Application Areas:Electrical field Electronic field Automotive sector
Color:--
Grade:Light diffusion level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.15	%
Melt flow rate	300°C/1.2 kg	ASTM D1238	40	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	38.0	cm3/10min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Bending stress	-- 5, 6	ISO 178	91.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 4	ASTM D790	100	Mpa
Tensile strength	Yield 3	ASTM D638	60.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		Tensile strength	Break 3	ASTM D638	56.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	56.0	Mpa
Tensile modulus	-- 2	ASTM D638	2270	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2180	Mpa
elongation	Yield 3	ASTM D638	5.5	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break 3	ASTM D638	130	%
		elongation	elongation	Break	ISO 527-2/50	97	%
Bending modulus	50.0 mm Span 4	ASTM D790	2240	Mpa
Bending modulus	Bending modulus	-- 5	ISO 178	2180	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ASTM D152510	135	°C
	Vicat softening temperature	--	ISO 306/B50	129	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	130	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831, ISO 11359-2	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	8.0E-5	cm/cm/°C
RTI		UL 746	105	°C
RTI Imp		UL 746	105	°C
RTI Elec		UL 746	105	°C
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	121	°C
	Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	110	°C
	Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	115	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过

injection	Test Result	Unit
drying time	3.0 到 4.0	hr
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	240 到 280	°C
Temperature in the middle of the barrel	250 到 295	°C
Temperature at the front of the material cylinder	260 到 305	°C
Spray nozzle temperature	255 到 300	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	35 到 75	rpm
Exhaust hole depth	0.038 到 0.076	mm
drying temperature	105 到 110	°C
Processing (melt) temperature	260 到 305	°C
Mold temperature	50 到 80	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	56.0	J
Dart impact equipped with measuring instruments	Dart impact equipped with measuring instruments	--	ISO 6603-2	95.0	J
Impact strength of simply supported beam gap 7	-30°C	ISO 179/1eA	13	kJ/m²
Impact strength of simply supported beam gap 7	Impact strength of simply supported beam gap 7	23°C	ISO 179/1eA	64	kJ/m²
The impact strength of a simply supported beam without a notch is 7	-30°C	ISO 179/1eU	无断裂
	The impact strength of a simply supported beam without a notch is 7	23°C	ISO 179/1eU	无断裂
Unscented Izod Impact Strength 8	-30°C	ISO 180/1U	无断裂
Unscented Izod Impact Strength 8	Unscented Izod Impact Strength 8	23°C	ISO 180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	120

optical performance	Test Condition	Test Method	Test Result	Unit
transmissivity	2540 µm	ASTM D1003	88.0	%
Haze	2540 µm	ASTM D1003	< 1.0	%
Refractive index		ASTM D542	1.582

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.30 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.0 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.