Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50到0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Water absorption rate | Equilibrium,23°C | ASTMD570 | 0.35 | % |
| Water absorption rate | Equilibrium,100°C | ASTMD570 | 0.58 | % |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 11 | g/10min |
| Specific volume | | ASTMD792 | 0.830 | cm³/g |
| Density/specific gravity | -- | ASTMD792 | 1.20 | g/cm³ |
| Density/specific gravity | -- | ASTMD792 | 1.19 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength 1 | Break | ASTMD638 | 68.0 | Mpa |
| Tensile strength 1 | Yield | ASTMD638 | 62.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Bending modulus 3 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Elongation rate 2 | Yield | ASTMD638 | 7.0 | % |
| Elongation rate 2 | Break | ASTMD638 | 130 | % |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 96.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTMD15256 | 154 | °C |
| RTI | | UL746 | 130 | °C |
| specific heat | | ASTMC351 | 1250 | J/kg/°C |
| thermal conductivity | | ASTMC177 | 0.27 | W/m/K |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 137 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 132 | °C |
| RTIElec | | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 60Hz | ASTMD150 | 9E-04 | |
| Dissipation factor | 1MHz | ASTMD150 | 0.010 | |
| Dielectric constant | 50Hz | ASTMD150 | 3.17 | |
| Dielectric constant | 60Hz | ASTMD150 | 3.17 | |
| Dielectric constant | 1MHz | ASTMD150 | 2.96 | |
| Volume resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Hot wire ignition | HWI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC1 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 3200 | J/m |
| Tensile impact strength 5 | | ASTMD1822 | 577 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 800 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 70 | |
| Rockwell hardness | R-Scale | ASTMD785 | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| Refractive index | | ASTMD542 | 1.586 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ASTMD2863 | 25 | % |
| UL flame retardant rating | 1.47mm | UL94 | V-2 | |
| UL flame retardant rating | 5.99mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.