Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance High temperature resistan transparent High mobility
Application Areas:--
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	300°C/1.2 kg	ASTM D1238	22	g/10 min
Molten Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	21.0	cm3/10min
Shrinkage rate - flow	-- 2	内部方法	0.50 到 0.70	%
Shrinkage rate - flow	Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.35	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 3	ASTM D638	2350	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2350	Mpa
Tensile strength	Yield 4	ASTM D638	63.0	Mpa
Tensile strength	Tensile strength	Yield	ISO 527-2/50	63.0	Mpa
elongation	Yield 4	ASTM D638	6.0	%
	elongation	Yield	ISO 527-2/50	6.0	%
		elongation	Break 4	ASTM D638	> 70	%
		elongation	elongation	Break	ISO 527-2/50	> 70	%
Bending modulus	50.0 mm Span 5	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	-- 6	ISO 178	2300	Mpa
Bending stress	-- 6, 7	ISO 178	90.0	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 5	ASTM D790	90.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	133	°C
	Thermal deformation temperature under load	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Bf	133	°C
		Thermal deformation temperature under load	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	122	°C
		Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	122	°C
Vicat softening temperature		ISO 306/B50, ASTM D152510	140	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion - flow	-40 to 95°C	ASTM E831	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion - flow	Linear coefficient of thermal expansion - flow	23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
thermal conductivity		ASTM C177, ISO 8302	0.20	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTM D257, IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	1.60 mm	ASTM D149, IEC 60243-1	27	KV/mm
Dielectric constant	60 Hz	ASTM D150, IEC 60250	3.00
Dielectric constant	Dielectric constant	1 MHz	ASTM D150, IEC 60250	3.00
Dissipation factor	60 Hz	ASTM D150, IEC 60250	1.0E-3
Dissipation factor	Dissipation factor	1 MHz	ASTM D150, IEC 60250	0.010

injection	Test Result	Unit
drying temperature	120	°C
drying time	2.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Hopper temperature	60 到 80	°C
Temperature at the rear of the barrel	260 到 280	°C
Temperature in the middle of the barrel	270 到 290	°C
Temperature at the front of the material cylinder	280 到 300	°C
Spray nozzle temperature	270 到 290	°C
Processing (melt) temperature	280 到 300	°C
Mold temperature	80 到 100	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Non notched cantilever beam impact	23°C	ASTM D4812, ISO 180/1U	无断裂
Non notched cantilever beam impact	Non notched cantilever beam impact	-30°C 8	ISO 180/1U	无断裂
Dart impact equipped with measuring instruments	23°C, Energy at Peak	ASTM D3763	55.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTM D785	120
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	120

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ISO 179/leA	1.586
transmissivity	2540 µm	ASTM D1003	88.0 到 90.0	%
Haze	2540 µm	ASTM D1003	< 0.80	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.