PC Makrolon® 2400 COVESTRO GERMANY

136

Unit Price:
$2177 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
36MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low viscosity
Application Areas:Electrical applications Industrial applications Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Volume density		ISO 60	0.66	g/cc
Balanced moisture absorption		ISO 62	0.12	%
Water absorption rate		ISO 62	0.3	%
Water vapor permeability		ISO 15106-1	15	g/m2
Linear forming shrinkage rate	Flow	ISO 294-4	0.0065	cm/cm
Horizontally		ISO 294-4	0.0065	cm/cm

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO 2039-1	113	Mpa
Tensile strength	Break50 mm/min	ISO 527-1,-2	70	Mpa
Tensile strength	Tensile strength	Yield50 mm/min	ISO 527-1,-2	65	Mpa
Elongation rate	Break50 mm/min	ISO 527-1,-2	>= 50	%
	Elongation rate	50 mm/min	ISO 527-1,-2	120	%
	Elongation rate	Elongation rate	Yield50 mm/min	ISO 527-1,-2	6.3	%
Tensile modulus	1 mm/min	ISO 527-1,-2	2.35	GPa
Bending strength	2 mm/min	ISO 178	96	Mpa
Bending strength	Bending strength	2 mm/min	ISO 178	72	Mpa
Bending modulus	2 mm/min	ISO 178	2.35	GPa
Tensile creep modulus	1 hr	ISO 899-1	2200	Mpa
Tensile creep modulus	Tensile creep modulus	1000 hr	ISO 899-1	1900	Mpa

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC 60093	10000000000000000	ohm·cm
Surface resistivity		IEC 60093	10000000000000000	Ohm
Dielectric constant		IEC 60250	3.1
Dielectric constant	Dielectric constant		IEC 60250	3
Dielectric strength		IEC 60243-1	34	KV/mm
Dissipation factor		IEC 60250	0.009
Dissipation factor	Dissipation factor		IEC 60250	0.00050
Compared to the leakage trace index		IEC 60112	250 V
Compared to the leakage trace index	Compared to the leakage trace index		IEC 60112	125 V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of cantilever beam gap		ISO 180/1A	75	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	12	kJ/m²
Impact strength of simply supported beam without notch		ISO 179/1eU	NB	NB
Impact strength of simply supported beam gap		ISO 179/1eA	6.5
Impact strength of simply supported beam gap	Impact strength of simply supported beam gap		ISO 179/1eA	1.4

Flame retardant performance	Test Condition	Test Method	Test Result	Unit
Flammability index of heating wire		IEC 60695-2-12	850	°C
Flammability index of heating wire	Flammability index of heating wire		IEC 60695-2-13	875	°C

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion - flow		ISO 11359-1,-2	65	µm/m-°C
Linear coefficient of thermal expansion, lateral flow		ISO 11359-1,-2	65	µm/m-°C
Thermal conductivity coefficient		ISO 8302	0.2	W/m/K
Thermal deformation temperature under load	0.46 MPa	ISO 75-1,-2	139	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa	ISO 75-1,-2	127	°C
Vicat softening temperature		ISO 306	147	°C
Vicat softening temperature	Vicat softening temperature		ISO 306	148	°C
Glass transition temperature, Tg	10°C/min	ISO 11357-1,-2	147	°C
Flammability		UL94	HB
Flammability	Flammability		UL94	V-2
Extreme Oxygen Index		ISO 4589-2	27	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.