PC Makrolon® 9415 000000 COVESTRO GERMANY
146
Unit Price:$3383 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber reinf 10% filler by weight 10% filler by weight
- Application Areas:Fiber grade
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | TD | ISO2577 | 0.40to0.60 | % |
| MD | ISO2577 | 0.40to0.60 | % | |
| TD:2.00mm3 | ISO294-4 | 0.45 | % | |
| MD:2.00mm3 | ISO294-4 | 0.60 | % | |
| 吸水率 | 饱和,23°C | ISO62 | 0.26 | % |
| 平衡,23°C,50%RH | ISO62 | 0.10 | % | |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 7.0 | g/10min |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| 密度 / 比重 | 23°C | ISO1183 | 1.27 | g/cm³ |
| 表观密度2 | ISO60 | 0.64 | g/cm³ |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲应变5 | 23°C | ISO178 | 5.8 | % |
| 弯曲应力4 | 3.5%Strain,23°C | ISO178 | 95.0 | Mpa |
| 23°C | ISO178 | 105 | Mpa | |
| 弯曲模量4 | 23°C | ISO178 | 3600 | Mpa |
| TensileCreepModulus | 1hr | ISO899-1 | 3600 | Mpa |
| 拉伸应力 | 屈服,23°C | ISO527-2/5 | 64.0 | Mpa |
| 断裂,23°C | ISO527-2/5 | 45.0 | Mpa | |
| 拉伸应变 | 屈服,23°C | ISO527-2/5 | 4.4 | % |
| 断裂,23°C | ISO527-2/5 | 15 | % | |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | 2900 | Mpa |
| 拉伸模量 | 23°C | ISO527-2/1 | 3800 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 142 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 136 | °C | |
| BallPressureTest | 137°C | IEC60695-10-2 | Pass | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTIImp | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| 维卡软化温度 | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| 线形热膨胀系数 | MD：23到55°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| 导热系数8 | 23°C | ISO8302 | 0.22 | W/m/K |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | 23°C,1.00mm | IEC60243-1 | 36 | KV/mm |
| 耗散因数 | 23°C,100Hz | IEC60250 | 1E-03 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| 相对电容率 | 23°C,100Hz | IEC60250 | 3.20 | |
| 23°C,1MHz | IEC60250 | 3.20 | ||
| 漏电起痕指数 | 解决方案A | IEC60112 | 175 | V |
| 解决方案B | IEC60112 | 125 | V | |
| 表面电阻率 | IEC60093 | 1E+16 | ohms | |
| 体积电阻率 | 23°C | IEC60093 | 1E+16 | ohms·cm |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁无缺口冲击强度 | -60°C,CompleteBreak | ISO179/1eU | 100 | kJ/m² |
| -30°C,完全断裂 | ISO179/1eU | 120 | kJ/m² | |
| 23°C,完全断裂 | ISO179/1eU | 150 | kJ/m² | |
| 多轴向仪器化冲击能量 | -30°C | ISO6603-2 | 15.0 | J |
| 23°C | ISO6603-2 | 25.0 | J | |
| CharpyNotchedImpactStrength6 | 23°C,CompleteBreak | ISO7391 | 10 | kJ/m² |
| NotchedIzodImpactStrength7 | 23°C,CompleteBreak | ISO7391 | 10 | kJ/m² |
| 多轴向仪器化冲击力峰值 | -30°C | ISO6603-2 | 3700 | N |
| 23°C | ISO6603-2 | 4000 | N |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 球压硬度 | ISO2039-1 | 128 | Mpa |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 极限氧指数9 | ISO4589-2 | 35 | % | |
| ApplicationofFlamefromSmallBurner | 2.00mm | DIN4102 | B2 | |
| MethodKandF:2.00mm | DIN53438-1,-3 | K1,F1 | ||
| UL阻燃等级 | 0.75mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA | ||
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 960 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 900 | °C |
| 1.5mm | IEC60695-2-13 | 900 | °C | |
| 3.0mm | IEC60695-2-13 | 900 | °C | |
| 燃烧速率-US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| 针焰试验 | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| SelfIgnitionTemperature | ASTMD1929 | 550 | °C |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISOShortname | ISO7391-PC,MFR,(,,)-09-9,GF10 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.