PC LEXAN™ EXL9134 BK SABIC INNOVATIVE US
155
- Unit Price:
- $4000 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High ductility at low tem Short molding cycle
- Application Areas:Electronic and Electrical Electronic display Aerospace Applications Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.40 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % | |
| Outdoor applicability | UL 746C | f1 | ||
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 16 | g/10 min |
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 15.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.40 到 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2100 | Mpa |
| -- | ISO 527-2/1 | 2000 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 6.0 | % |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Break 3 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/50 | 110 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2400 | Mpa |
| -- 5 | ISO 178 | 2100 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 58.0 | Mpa |
| Yield | ISO 527-2/50 | 56.0 | Mpa | |
| Break 3 | ASTM D638 | 59.0 | Mpa | |
| Break | ISO 527-2/50 | 57.0 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 87.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 92.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI | UL 746 | 120 | °C | |
| RTI Imp | UL 746 | 115 | °C | |
| RTI Elec | UL 746 | 125 | °C | |
| Vicat softening temperature | -- | ASTM D152510 | 140 | °C |
| -- | ISO 306/B50 | 139 | °C | |
| -- | ISO 306/B120 | 141 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 6.1E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.2E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 6.2E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 123 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9 | ISO 75-2/Af | 118 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 270 到 295 | °C | ||
| Temperature in the middle of the barrel | 280 到 305 | °C | ||
| Temperature at the front of the material cylinder | 295 到 315 | °C | ||
| Spray nozzle temperature | 290 到 310 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm | ||
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 295 到 315 | °C | ||
| Mold temperature | 70 到 95 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 35 | kJ/m² |
| 23°C | ISO 179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unscented Izod Impact Strength 8 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 67.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA | ||
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 825 | °C |
| 3.0 mm | IEC 60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.