PC LEXAN™ HP2-1H111 SABIC INNOVATIVE US
122
- Unit Price:
- $5274 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine medical care
- Color:--
- Grade:Medical grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Equilibrium,23°C | ASTMD570 | 0.35 | % | |
| Equilibrium,100°C | ASTMD570 | 0.58 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 18 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 16.0 | cm3/10min |
| Specific volume | ASTMD792 | 0.830 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 5 | ISO178 | 2300 | Mpa | |
| Elongation rate 4 | Break | ASTMD638 | 130 | % |
| Bending strength 5,6 | ISO178 | 90.0 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 7.0 | % |
| Tensile modulus 2 | ASTMD638 | 2370 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 68.0 | Mpa |
| Yield | ASTMD638 | 62.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 96.0 | Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile modulus | ISO527-2/1 | 2350 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Break | ISO527-2/50 | 65.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Break | ISO527-2/50 | 100 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 130 | °C | |
| RTIStr | UL746 | 130 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 129 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 137 | °C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat softening temperature | ASTMD152510 | 154 | °C | |
| -- | ISO306/B50 | 140 | °C | |
| -- | ISO306/B120 | 141 | °C | |
| specific heat | ASTMC351 | 1250 | J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 | W/m/K | |
| ISO8302 | 0.20 | W/m/K | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 122 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC1 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC2 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 2.70 | |
| 60Hz | IEC60250 | 2.70 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric constant | 50Hz | ASTMD150 | 3.17 | |
| 60Hz | ASTMD150 | 3.17 | ||
| 1MHz | ASTMD150 | 2.96 | ||
| Volume resistivity | ASTMD257 | >1.0E+17 | ohms·cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| 1MHz | ASTMD150 | 0.010 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 62.0 | J |
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Suspended wall beam gap impact strength 7 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 12 | kJ/m² | |
| Tensile impact strength 8 | ASTMD1822 | 546 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 70 | |
| R-Sale | ASTMD785 | 118 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.586 | ||
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Extreme Oxygen Index | ISO4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.