PC LEXAN™ 500ECR-131 SABIC INNOVATIVE NANSHA
135
- Unit Price:
- $2820 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 74.3MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Flame retardant Glass fiber reinforced
- Application Areas:Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molding shrinkage rate | ASTM D955 | % | 0.4－0.6 | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | g/10min | 300℃/1.2kg,7.5 | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | % | 0.31 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in²] | 479000 | |
| tensile strength | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in²] | 8270/6960 | |
| elongation | ASTM D638/ISO 527 | % | ||
| Bending modulus | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in²] | 453000（493000） | |
| bending strength | ASTM D790/ISO 178 | kg/cm²(MPa)[Lb/in²] | 1360（13800） |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 干燥温度：248℉，干燥时间：2.0to4.0 hr | |||
| Processing temperature | ℃ | 518-572 | ||
| ℃ | 554-608 | |||
| ℃ | 536-590 | |||
| Mold temperature | ℃ | 176-248 | ||
| Melt Temperature | ℃ | 554-608 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy impact strength | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 44565 | |
| IZOD notch impact strength | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 缺口：2.5 | |
| ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 缺口：1.9 | ||
| ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | 44570 | ||
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257/IEC 60093 | Ω | >1.0E+15 ohms | |
| Dielectric constant | ASTM D150/IEC 60250 | 50HZ/60HZ:2.9 | ||
| ASTM D150/IEC 60250 | 2.8 | |||
| Dielectric loss | ASTM D150/IEC 60250 | 0.001 | ||
| ASTM D150/IEC 60250 | 0.01 | |||
| Volume resistivity | ASTM D257/IEC 60093 | Ω.cm | >1.0E+15 ohm.cm |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V1-V0 | ||
| vicat softening point | ASTM D1525/ISO R306 | ℃（℉） | 309 | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | mm/mm.℃ | 0.000026－0.000047 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.