PC LEXAN™ HPS1-1125 SABIC INNOVATIVE US
115
- Unit Price:
- $8227 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:medicine medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.15 | % |
| Equilibrium,23°C | ASTMD570 | 0.35 | % | |
| Equilibrium,100°C | ASTMD570 | 0.58 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 25 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 23.0 | cm3/10min |
| Specific volume | ASTMD792 | 0.835 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 5 | ISO178 | 2300 | Mpa | |
| Bending strength 5,6 | ISO178 | 90.0 | Mpa | |
| Tensile modulus 2 | ASTMD638 | 2380 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 62.1 | Mpa |
| Break | ASTMD638 | 65.5 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2310 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 93.1 | Mpa |
| Elongation rate 4 | Break | ASTMD638 | 120 | % |
| Elongation rate 3 | Yield | ASTMD638 | 6.0 | % |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 10.0 | mg |
| Tensile stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Break | ISO527-2/50 | 50.0 | Mpa | |
| Tensile strain | Break | ISO527-2/50 | 70 | % |
| Yield | ISO527-2/50 | 6.0 | % | |
| Tensile modulus | ISO527-2/1 | 2350 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 127 | °C | |
| Linear coefficient of thermal expansion | MD：-40to95°C | ASTME831 | 6.8E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| specific heat | ASTMC351 | 1260 | J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.19 | W/m/K | |
| ISO8302 | 0.20 | W/m/K | ||
| Vicat softening temperature | -- | ISO306/B50 | 139 | °C |
| -- | ISO306/B120 | 140 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 10 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 133 | °C |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 121 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inAir | ASTMD149 | 15 | KV/mm |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 2.70 | |
| 60Hz | IEC60250 | 2.70 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Dielectric constant | 50Hz | ASTMD150 | 3.17 | |
| 60Hz | ASTMD150 | 3.17 | ||
| 1MHz | ASTMD150 | 2.96 | ||
| Volume resistivity | ASTMD257 | >1.0E+17 | ohms·cm | |
| IEC60093 | >1.0E+15 | ohms·cm | ||
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| 1MHz | ASTMD150 | 0.010 | ||
| 50Hz | IEC60250 | 1E-03 | ||
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 23°C | ASTMD3029 | 169 | J |
| Tensile impact strength 9 | ASTMD1822 | 378 | kJ/m² | |
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 12 | kJ/m² | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 12 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 54.2 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ASTMD785 | 70 | |
| R-Sale | ASTMD785 | 118 | ||
| Ball pressure hardness | H358/30 | ISO2039-1 | 95.0 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ASTMD542 | 1.586 | ||
| Haze | 2540µm | ASTMD1003 | 1.0 | % |
| transmissivity | 2540µm | ASTMD1003 | 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index | ISO4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.