PC LEXAN™ PK2870-21317 SABIC INNOVATIVE US
130
- Unit Price:
- $2296 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance wear resistant
- Application Areas:packing Fiber grade
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | equilibriu | ASTM D570 | 0.58 | |
| equilibriu | ASTM D570 | 0.35 | ||
| 23°C/sat | ISO 62 | 0.35 | ||
| Moisture absorption rate | 23°C / 50 | ISO 62 | 0.15 | |
| Melt Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 2 | cm³/10 min |
| 300°C/2.16 kg | ISO 1133 | 4 | cm³/10 min | |
| Melt Mass Flow Rate (MFR) | / | 2.5 | g/10min | |
| Longitudinal shrinkage rate (Flow) | flow, 3. | Internal | 0.5~0.7 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength yield (yld) | 1.3 mm/min/ | ASTM D790 | 95 | Mpa |
| 2 mm/ | ISO 178 | 95 | Mpa | |
| Tensile elongation yield (yld) | Type I, 5 | ASTM D638 | 7 | % |
| 50 mm/m | ISO 527 | 7 | % | |
| Bending modulus | 2 mm/mi | ISO 178 | 2300 | Mpa |
| 1.3 mm/min | ASTM D790 | 2300 | Mpa | |
| Tensile strength yield (yld) | Type I, 5 | ASTM D638 | 62 | Mpa |
| 50 mm/m | ISO 527 | 65 | Mpa | |
| Tensile strength fracture (brk) | 50 mm/m | ISO 527 | 70 | Mpa |
| Type I, 50 | ASTM D638 | 65 | Mpa | |
| Tensile elongation fracture (brk) | Type I, 5 | ASTM D638 | 70 | % |
| 50 mm/m | ISO 527 | 70 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Izod Unnotched at 23 ℃ (73 ℉) | 80*10*3 | ISO 180/1A | 75 | kJ/m² |
| Charpy Notched -30 ℃ (-22 ℉) | V-notch Edgew | ISO 179/1eA | 50 | kJ/m² |
| Charpy Notched at 23 ℃ (73 ℉) | V-notch Edgew | ISO 179/1eA | 70 | kJ/m² |
| Izod Notched on Cantilever Beam | / | ASTM D256 | 150 | J/m |
| Izod Unnotched -30 ℃ (-22 ℉) | 80*10*3 | ISO 180/1A | 55 | kJ/m² |
| Izod Notched at 23 ℃ (73 ℉) | ASTM D256 | 750 | J/m | |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | ASTM D 4812 | NB | J/m | |
| 80*10*3 | ISO 180/1U | NB | kJ/m² | |
| Falling hammer impact | ASTM D 3029 | 170 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness R | 120 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 2.54 mm | ASTM D1003 | 88 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | Rate B/5 | ASTM D1525 | 150 | °C |
| Rate B/5 | ISO 306 | 150 | °C | |
| Rate B/5 | ISO 306 | 149 | °C | |
| Specific heat capacity | ASTM C 351 | 1.25 | J/g-°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.