PC LEXAN™ EXL1414T NA8A005T SABIC INNOVATIVE US
139
Unit Price:$3730 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low temperature resistanc transparent Processability Moderate liquidity Ductility copolymer
- Application Areas:Electrical field Electronic field Household appliances Household appliances Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 | % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 | % | |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.12 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.090 | % | |
| 熔流率（熔体流动速率） | 300°C/1.2 kg | ASTM D1238 | 10 | g/10 min |
| 熔融体积流量（MVR） | 300°C/1.2 kg | ISO 1133 | 9.00 | cm3/10min |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -- 2 | ASTM D638 | 2180 | Mpa |
| -- | ISO 527-2/1 | 2300 | Mpa | |
| 伸长率 | 屈服 3 | ASTM D638 | 5.6 | % |
| 屈服 | ISO 527-2/50 | 5.4 | % | |
| 断裂 3 | ASTM D638 | 120 | % | |
| 断裂 | ISO 527-2/50 | 110 | % | |
| 弯曲模量 | 50.0 mm 跨距 4 | ASTM D790 | 2180 | Mpa |
| -- 5 | ISO 178 | 2120 | Mpa | |
| 抗张强度 | 屈服 3 | ASTM D638 | 57.0 | Mpa |
| 屈服 | ISO 527-2/50 | 56.0 | Mpa | |
| 断裂 3 | ASTM D638 | 59.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 55.0 | Mpa | |
| 弯曲应力 | -- 5, 6 | ISO 178 | 88.0 | Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 92.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化温度 | -- | ASTM D152510, ISO 306/B5010 | 138 | °C |
| -- | ISO 306/B120 | 139 | °C | |
| 载荷下热变形温度 | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9 | ISO 75-2/Af | 116 | °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 线形热膨胀系数 | 流动 : -40 到 95°C | ASTM E831 | 6.7E-5 | cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C | |
| 横向 : -40 到 95°C | ASTM E831 | 8.0E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| RTI | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | ASTM D257 | > 1.0E+15 | ohms | |
| 体积电阻率 | ASTM D257 | > 1.0E+15 | ohms·cm |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 加工（熔体）温度 | 295 到 315 | °C | ||
| 模具温度 | 70 到 95 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 270 到 295 | °C | ||
| 料筒中部温度 | 280 到 305 | °C | ||
| 料筒前部温度 | 295 到 315 | °C | ||
| 射嘴温度 | 290 到 310 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 装有测量仪表的落镖冲击 | -30°C, Total Energy | ASTM D3763 | 77.0 | J |
| 23°C, Total Energy | ASTM D3763 | 75.0 | J | |
| 简支梁缺口冲击强度 7 | -30°C | ISO 179/1eA | 60 | kJ/m² |
| 23°C | ISO 179/1eA | 70 | kJ/m² | |
| 简支梁无缺口冲击强度 7 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| 无缺口伊佐德冲击强度 8 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | L 计秤 | ISO 2039-2 | 87 |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 雾度 | 2540 µm | ASTM D1003 | 3.0 | % |
| 透射率 | 2540 µm | ASTM D1003 | 82.0 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 灼热丝易燃指数 | 3.0 mm | IEC 60695-2-12 | 960 | °C |
| 热灯丝点火温度 | 0.8 mm | IEC 60695-2-13 | 850 | °C |
| 3.0 mm | IEC 60695-2-13 | 850 | °C | |
| UL 阻燃等级 | 0.8 mm | UL 94 | HB | |
| 3.0 mm | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.