PC LEXAN™ 103R-111 SABIC INNOVATIVE SPAIN

145

Unit Price:
$1784 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:transparent UV resistance Weather resistance
Application Areas:Outdoor applications Lighting fixtures
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Specific volume		ASTM D792	0.830	cm³/g
Melt flow rate	300°C/1.2 kg	ASTM D1238	7.0	g/10 min
Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	24 hr	ASTM D570	0.15	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Outdoor applicability		UL 746C	f1

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength 2	Yield	ASTM D638	62.0	Mpa
Tensile strength 2	Tensile strength 2	Break	ASTM D638	65.0	Mpa
Elongation rate 2	Yield	ASTM D638	7.0	%
Elongation rate 2	Elongation rate 2	Break	ASTM D638	110	%
Bending modulus	50.0 mm Span	ASTM D790	2340	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	93.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg

Thermal performance	Test Condition	Test Method	Test Result	Unit
Thermal deformation temperature under load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Thermal deformation temperature under load	Thermal deformation temperature under load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
Vicat softening temperature		ASTM D15255	154	°C
Linear coefficient of thermal expansion - flow	-40 to 95°C	ASTM E831	6.8E-5	cm/cm/°C
specific heat		ASTM C351	1250	J/kg/°C
thermal conductivity		ASTM C177	0.19	W/m/K
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI		UL 746	130	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	50 kHz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.96
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.010
Compared to the Leakage Tracking Index (CTI)		UL 746	PLC 2
High arc combustion index (HAI) 6		UL 746	PLC 1
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 2
Hot wire ignition (HWI)		UL 746	PLC 4

injection	Test Result	Unit
drying temperature	120	°C
drying time	3.0 到 4.0	hr
Suggested maximum moisture content	0.020	%
Suggested injection volume	40 到 60	%
Temperature at the rear of the barrel	290 到 310	°C
Temperature in the middle of the barrel	300 到 320	°C
Temperature at the front of the material cylinder	310 到 330	°C
Spray nozzle temperature	305 到 325	°C
Processing (melt) temperature	310 到 330	°C
Mold temperature	80 到 115	°C
Back pressure	0.300 到 0.700	Mpa
Screw speed	40 到 70	rpm
Exhaust hole depth	0.025 到 0.076	mm

Impact performance	Test Condition	Test Method	Test Result	Unit
Non notched cantilever beam impact	23°C	ASTM D4812	3200	J/m
Falling hammer impact	23°C	ASTM D3029	169	J
Tensile impact strength 4		ASTM D1822	546	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ASTM D542	1.586
transmissivity	2540 µm	ASTM D1003	88.0	%
Haze	2540 µm	ASTM D1003	1.0	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.76 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.