PC IUPILON™ GSH2030R2 MITSUBISHI ENGINEERING JAPAN
198
- Unit Price:
- $6839 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% filler by weight
- Application Areas:electrical equipment Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 0.050to0.25 | % | |
| 吸水率(Saturation,23°C) | 0.090 | % | ||
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 5.7 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 4.80 | cm3/10min |
| Shrinkage rate | TD:3.20mm | 0.25to0.45 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 8900 | Mpa | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.5 | % |
| Bending modulus | ISO178 | 8500 | Mpa | |
| Bending stress | ISO178 | 180 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 148 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 144 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 2E+15 | ohms | |
| Volume resistivity | IEC60093 | 2E+16 | ohms·cm | |
| Dielectric strength | 1.00mm | IEC60243-1 | 32 | KV/mm |
| 3.00mm | IEC60243-1 | 20 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.60 | |
| 1MHz | IEC60250 | 3.50 | ||
| Dissipation factor | 100Hz | IEC60250 | 1.1E-03 | |
| 1MHz | IEC60250 | 8.4E-03 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 50 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.