PC LEXAN™ 121R-111 SABIC INNOVATIVE SPAIN
146
- Unit Price:
- $2243 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 73MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity transparent
- Application Areas:building materials Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 21.0 | cm3/10min |
| Shrinkage rate - Flow 2 | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.35 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2350 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 63.0 | Mpa |
| Break | ISO 527-2/50 | 65.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2/50 | 6.0 | % |
| Break | ISO 527-2/50 | 100 | % | |
| Bending modulus 3 | ISO 178 | 2300 | Mpa | |
| Bending stress 3, 4 | ISO 178 | 90.0 | Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | 内部方法 | 10.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 7 | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 133 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 122 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 140 | °C |
| -- | ISO 306/B120 | 141 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion - transverse | 23 to 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.20 | W/m/K | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 125 | °C | |
| RTI | UL 746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800 mm, in Oil | IEC 60243-1 | 35 | KV/mm |
| 1.60 mm, in Oil | IEC 60243-1 | 27 | KV/mm | |
| 3.20 mm, in Oil | IEC 60243-1 | 17 | KV/mm | |
| Relative permittivity | 50 Hz | IEC 60250 | 2.70 | |
| 60 Hz | IEC 60250 | 2.70 | ||
| 1 MHz | IEC 60250 | 2.70 | ||
| Dissipation factor | 50 Hz | IEC 60250 | 1.0E-3 | |
| 60 Hz | IEC 60250 | 1.0E-3 | ||
| 1 MHz | IEC 60250 | 0.010 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 260 到 280 | °C | ||
| Temperature in the middle of the barrel | 270 到 290 | °C | ||
| Temperature at the front of the material cylinder | 280 到 300 | °C | ||
| Spray nozzle temperature | 270 到 290 | °C | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Mold temperature | 80 到 100 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Simply supported beam without notch impact strength 5 | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Suspended wall beam notch impact strength 6 | -30°C | ISO 180/1A | 11 | kJ/m² |
| 23°C | ISO 180/1A | 65 | kJ/m² | |
| Unscented Izod Impact Strength 6 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H 358/30 | ISO 2039-1 | 95.0 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index | ISO 489 | 1.586 | ||
| transmissivity | 2540 µm | ASTM D1003 | 88.0 到 90.0 | % |
| Haze | 2540 µm | ASTM D1003 | < 0.80 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.70 mm | UL 94 | HB | |
| 3.0 mm | UL 94 | HB | ||
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 850 | °C |
| Extreme Oxygen Index | ISO 4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.