PC LEXAN™ 221R-111 SABIC INNOVATIVE NANSHA
176
Unit Price:$2720 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 82MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent Flame retardant enhance
- Application Areas:Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 特定体积 | ASTM D792 | 0.830 | cm³/g | |
| 室外适用性 | UL 746C | f2 | ||
| 吸水率 | 24 hr | ASTM D570 | 0.15 | % |
| 平衡, 23°C | ASTM D570 | 0.35 | % | |
| 平衡, 100°C | ASTM D570 | 0.58 | % | |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 熔体质量流动速率 | 300°C/1.2 kg | ASTM D1238 | 18 | g/10 min |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 装有测量仪表的落镖冲击 | 23°C, Energy at Peak | ASTM D3763 | 62.0 | J |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m |
| 拉伸冲击强度 | ASTM D1822 | 546 | kJ/m² | |
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 | mg |
| 落锤冲击 | 23°C | ASTM D3029 | 169 | J |
| 拉伸强度 | 屈服 | ASTM D638 | 62.0 | Mpa |
| 断裂 | ASTM D638 | 68.0 | Mpa | |
| 伸长率 | 屈服 | ASTM D638 | 7.0 | % |
| 断裂 | ASTM D638 | 130 | % | |
| 洛氏硬度 | M 级 | ASTM D785 | 70 | |
| R 级 | ASTM D785 | 118 | ||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 2340 | Mpa |
| 弯曲强度 | 屈服, 50.0 mm 跨距 | ASTM D790 | 96.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 | °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 129 | °C | |
| 维卡软化点 | ASTM D15255 | 154 | °C | |
| 比热 | ASTM C351 | 1250 | J/kg/°C | |
| 导热系数 | ASTM C177 | 0.25 | W/m/K | |
| RTI | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| 线形热膨胀系数 - 流动 | -40 到 95°C | ASTM E831 | 6.8E-5 | cm/cm/°C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 2 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 2 | ||
| 耗散因数 | 50 Hz | ASTM D150 | 9.0E-4 | |
| 60 Hz | ASTM D150 | 9.0E-4 | ||
| 1 MHz | ASTM D150 | 0.010 | ||
| 介电强度 | 3.20 mm, in Air | ASTM D149 | 15 | KV/mm |
| 高电弧燃烧指数(HAI) | UL 746 | PLC 1 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 2 | ||
| 介电常数 | 60 Hz | ASTM D150 | 3.17 | |
| 50 kHz | ASTM D150 | 3.17 | ||
| 1 MHz | ASTM D150 | 2.96 | ||
| 体积电阻率 | ASTM D257 | > 1.0E+17 | ohms·cm |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 加工（熔体）温度 | 280 到 305 | °C | ||
| 模具温度 | 70 到 95 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 260 到 280 | °C | ||
| 料筒中部温度 | 270 到 295 | °C | ||
| 料筒前部温度 | 280 到 305 | °C | ||
| 射嘴温度 | 275 到 300 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 透光率 | 2540 µm | ASTM D1003 | 88.0 | % |
| 折射率 | ASTM D542 | 1.586 | ||
| 雾度 | 2540 µm | ASTM D1003 | 1.0 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.1 mm | UL 94 | V-2 | |
| 6.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.