PC LEXAN™ EXL1414 SABIC INNOVATIVE NANSHA
129
- Unit Price:
- $3384 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Moderate liquidity Ductility copolymer Good demolding performanc
- Application Areas:Electrical applications Home appliance components Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.18 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ | ||
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 2 | ASTMD638 | 2020 | Mpa | |
| Tensile modulus | ISO527-2/1 | 2150 | Mpa | |
| Tensile strength 3 | Yield | ASTMD638 | 55.5 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 57.0 | Mpa |
| Tensile strength 3 | Break | ASTMD638 | 50.3 | Mpa |
| Tensile stress | Break | ISO527-2/50 | 60.0 | Mpa |
| Elongation rate 3 | Yield | ASTMD638 | 6.0 | % |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Elongation rate 4 | Break | ASTMD638 | 98 | % |
| Tensile strain | Break | ISO527-2/50 | 120 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 2230 | Mpa |
| Bending modulus 5 | ISO178 | 2250 | Mpa | |
| Bending strength 5,6 | ISO178 | 85.0 | Mpa | |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 92.4 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 139 | °C |
| Hot deformation temperature 9 | 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 140 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 128 | °C |
| Vicat softening temperature | ASTMD152510 | 145 | °C | |
| -- | ISO306/B50 | 145 | °C | |
| -- | ISO306/B120 | 146 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 120 | °C | |
| RTIStr | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,inOil | ASTMD149 | 16 | KV/mm |
| Dielectric constant | 100Hz | ASTMD150 | 2.68 | |
| 1MHz | ASTMD150 | 2.64 | ||
| Dissipation factor | 100Hz | ASTMD150 | 1.2E-03 | |
| 1MHz | ASTMD150 | 9.3E-03 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 65 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 770 | J/m |
| 23°C | ASTMD256 | 870 | J/m | |
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 60 | kJ/m² |
| 23°C | ISO180/1A | 70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | L-Sale | ASTMD785 | 89 | |
| R-Sale | ASTMD785 | 121 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | HB | |
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 850 | °C |
| 1.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 875 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.