Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity High temperature resistan
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 21.0 | cm3/10min |
| Modeling Shrinkage - Flow | 内部方法 | 0.50 到 0.70 | % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 | % | |
| Outdoor Suitability | UL 746C | f1 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 133 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 122 | °C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 140 | °C |
| Coefficient of Linear Thermal Expansion (Flow) | 23 到 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C |
| Thermal Conductivity | ISO 8302 | 0.20 | W/m/K | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 140°C 8 | IEC 60695-10-2 | 通过 | ||
| RTI Elec | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| Vicat Softening Temperature | -- | ISO 306/B120 | 141 | °C |
| RTI | UL 746 | 130 | °C |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Index of Refraction | ISO 489 | 1.586 | ||
| Transmittance | 2540 µm | ASTM D1003 | 88.0 到 90.0 | % |
| Haze | 2540 µm | ASTM D1003 | < 0.80 | % |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 3.0 mm | UL 94 | HB | |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 850 | °C |
| UL flame retardant rating | 0.75 mm | UL 94 | HB | |
| Oxygen Index | ISO 4589-2 | 25 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strain | 断裂 | ISO 527-2/50 | 100 | % |
| Tensile Stress | ISO 178 | 90.0 | Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 10.0 | mg |
| Flexural Modulus | ISO 178 | 2300 | Mpa | |
| Tensile Modulus | ISO 527-2/1 | 2350 | Mpa | |
| Tensile Stress | 断裂 | ISO 527-2/50 | 65.0 | Mpa |
| 屈服 | ISO 527-2/50 | 63.0 | Mpa | |
| Tensile Strain | 屈服 | ISO 527-2/50 | 6.0 | % |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Relative Permittivity | 60 Hz | IEC 60250 | 2.70 | |
| 50 Hz | IEC 60250 | 2.70 | ||
| Volume Resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 | KV/mm |
| Dissipation Factor? | 60 Hz | IEC 60250 | 1.0E-3 | |
| 50 Hz | IEC 60250 | 1.0E-3 | ||
| Relative Permittivity | 1 MHz | IEC 60250 | 2.70 | |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.010 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rear Temperature | 260 到 280 | °C | ||
| Middle Temperature | 270 到 290 | °C | ||
| Front Temperature | 280 到 300 | °C | ||
| Mold Temperature | 80 到 100 | °C | ||
| Processing (Melt) Temp | 280 到 300 | °C | ||
| Nozzle Temperature | 270 到 290 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Hopper Temperature | 60 到 80 | °C | ||
| Drying Temperature | 120 | °C | ||
| Drying Time | 2.0 到 4.0 | hr |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 95.0 | Mpa |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
| Notched Izod Impact Strength | -30°C | ISO 180/1A | 11 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 | |
| Notched Izod Impact Strength | 23°C | ISO 180/1A | 65 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 | |
| -30°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.