PC Makrolon® AL2447 COVESTRO SHANGHAI
154
- Unit Price:
- $2329 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance Flame retardant
- Application Areas:Automotive Applications Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density 3 | ISO60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 20 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 19.0 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.50到0.70 | % |
| MD | ISO2577 | 0.50到0.70 | % | |
| TD:2.00mm4 | ISO294-4 | 0.70 | % | |
| MD:2.00mm4 | ISO294-4 | 0.65 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/5 | 70.0 | Mpa | |
| Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/5 | 130 | % | |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Tensile creep modulus | 1hr | ISO899-1 | 2200 | Mpa |
| 1000hr | ISO899-1 | 1900 | Mpa | |
| Bending modulus 5 | 23°C | ISO178 | 2350 | Mpa |
| Bending stress 5 | 23°C | ISO178 | 98.0 | Mpa |
| 3.5%Strain,23°C | ISO178 | 74.0 | Mpa | |
| Bending strain 6 | 23°C | ISO178 | 7.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Glass transition temperature 9 | ISO11357-2 | 145 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| BallPressure Test | 135°C | IEC60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | MD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient 10 | 23°C | ISO8302 | 0.20 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 | °C |
| RTI | 1.5mm | UL746 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 18900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 4800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 630 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 160 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 3150 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 800 | cm³/m²/bar/24hr | |
| Water vapor permeability | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | 无断裂 | |
| -30°C | ISO179/1eU | 无断裂 | ||
| 23°C | ISO179/1eU | 无断裂 | ||
| Suspended wall beam gap impact strength 8 | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 55.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6000 | N |
| 23°C | ISO6603-2 | 5100 | N |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 115 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Refractive index 12 | ISO489 | 1.586 | ||
| transmissivity | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | >87.0 | % | |
| Haze | 3000µm | ISO14782 | <0.50 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index 11 | ISO4589-2 | 28 | % | |
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C | |
| UL flame retardant rating | 2.7mm | UL94 | HB | |
| 0.75mm | UL94 | V-2 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut | ISO7391-PC,MLR,(,, |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.