PC Makrolon® 2458 COVESTRO THAILAND
233
- Unit Price:
- $5386 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 188.4MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility Flame retardant High temperature resistan
- Application Areas:Electrical tools Household appliances Household appliances Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO2577 | 0.50to0.70 | % |
| MD | ISO2577 | 0.50to0.70 | % | |
| TD:2.00mm3 | ISO294-4 | 0.70 | % | |
| MD:2.00mm3 | ISO294-4 | 0.65 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 20 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 19.0 | cm3/10min |
| Density/specific gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
| Apparent density 2 | ISO60 | 0.66 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strain 5 | 23°C | ISO178 | 7.1 | % |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Bending stress 4 | 3.5%Strain,23°C | ISO178 | 73.0 | Mpa |
| 23°C | ISO178 | 97.0 | Mpa | |
| Bending modulus 4 | 23°C | ISO178 | 2350 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | 2200 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2/50 | 65.0 | Mpa |
| Break,23°C | ISO527-2/50 | 70.0 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2/50 | 6.1 | % |
| Break,23°C | ISO527-2/50 | 130 | % | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1900 | Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 139 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 145 | °C |
| -- | ISO306/B120 | 146 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| BallPressure Test | 138°C | IEC60695-10-2 | Pass | |
| Glass transition temperature 8 | ISO11357-2 | 146 | °C | |
| Thermal conductivity coefficient 9 | 23°C | ISO8302 | 0.20 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -60°C | ISO179/1eU | NoBreak | |
| -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | ||
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 55.0 | J | |
| Suspended wall beam gap impact strength 7 | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6000 | N |
| 23°C | ISO6603-2 | 5100 | N | |
| Impact strength of simply supported beam gap 6 | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 115 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | 87.0 | % | |
| Haze | 3000µm | ISO14782 | <0.80 | % |
| Refractive Index11 | ISO489 | 1.586 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| Extreme Oxygen Index 10 | ISO4589-2 | 28 | % | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO7391-PC,MR,(,,)-18-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.