Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.2 | |
| Melt index (flow coefficient) | | ASTM D1238/ISO 1133 | 10.5 | g/10min |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass Flow Rate (MFR) 300 ℃/1.2 kg | / | | 10.5 | g/10min |
| Longitudinal shrinkage rate (Flow) | flow, 3.2 | Internal | 0.5~0.7 | |
| Water absorption rate | 24 hours | ASTM D570 | 0.15 | |
| Water absorption rate | equilibriu | ASTM D570 | 0.58 | |
| Water absorption rate | equilibriu | ASTM D570 | 0.35 | |
| Bi Rong | / | | 0.83 | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength yield (yld) | Type I, 5 | ASTM D638 | 62 | Mpa |
| Tensile strength fracture (brk) | Type I, 5 | ASTM D638 | 68 | Mpa |
| Tensile elongation yield (yld) |
Type I, 5 | ASTM D638 | 7 | % |
| Tensile elongation fracture (brk) |
Type I, 5 | ASTM D638 | 130 | % |
| Bending strength yield (yld) | 1.3 mm/min/ | ASTM D790 | 96 | Mpa |
| Bending modulus | 1.3 mm/ | ASTM D790 | 2340 | Mpa |
| Rockwell hardness | | ASTM D785 | 118 | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustibility (rate) | | UL94 | HB | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Izod Notched at 23 ℃ (73 ℉) | | ASTM D256 | 801 | J/m |
| Cantilever beam without notch (Izod Unnotched) 23 ℃ (73 ℉) | / | | 3204 | J/m |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | / | | 63 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness M | | ASTM D 785 | 70 | |
| Rockwell hardness R | | | 118 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Light transmittance | 2.54 mm | ASTM D1003 | 88 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 154 | °C |
| Relative Temperature Index (RTI) impact w/impact- | | UL 746B | 130 | °C |
| Relative Temperature Index (RTI) Electrical Elec- | | UL 746B | 130 | °C |
| Relative Temperature Index (RTI) intensity w/o impact- | | UL 746B | 130 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.