PC CALIBRE™ 201-10 STYRON US
233
- Unit Price:
- $2889 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting transparent High impact resistance
- Application Areas:Fitness equipment Food containers Plastic toy
- Color:--
- Grade:Transparent level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Meltvolume-flowrate | 300°C/1.2kg | ISO11332 | 8.00 | cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 0.50to0.70 | % |
| Density/specific gravity | ISO1183/A | 1.20 | g/cm³ | |
| ISO11832 | 1200 | kg/m3 | ||
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Nominal strainatbreak | ISO527-22 | >50 | % | |
| Bending modulus 3 | ISO178 | 2400 | Mpa | |
| Bending stress 3 | ISO178 | 97.0 | Mpa | |
| Tensile modulus | ISO527-2/50 | 2300 | Mpa | |
| ISO527-22 | 2300 | Mpa | ||
| Tensile stress | Yield | ISO527-2/50 | 60.0 | Mpa |
| Yield | ISO527-22 | 60.0 | Mpa | |
| Break | ISO527-2/50 | 71.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 6.0 | % |
| Yield | ISO527-22 | 6.0 | % | |
| Break | ISO527-2/50 | 150 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa | ISO75-22 | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| 1.8MPa,Annealed | ISO75-2/A | 141 | °C | |
| 1.8MPa | ISO75-22 | 131 | °C | |
| Vicat softening temperature | ISO306/B50 | 149 | °C | |
| 50N | ISO3062 | 149 | °C | |
| Ball pressure temperature | IEC60335-1 | 125 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-22 | 7E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Annealed | ISO75-2/B | 144 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC600932 | >1.0E+13 | ohms·m | |
| Electrical strength | IEC60243-12 | 17 | KV/mm | |
| Relative permittivity | 100Hz | IEC602502 | 3.00 | |
| 1MHz | IEC602502 | 3.00 | ||
| Dissipation factor | 100Hz | IEC602502 | 1E-03 | |
| 1MHz | IEC602502 | 2E-03 | ||
| Leakage Trace Index | 2.00mm | IEC60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpynotchedimimpact string | 23°C | ISO179/1eA2 | 90.0 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA2 | 13.0 | kJ/m² |
| Charpy impact strength | 23°C | ISO179/1eU2 | NoBreak | |
| Charpyimpactstrength | -30°C | ISO179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO180/4A | 88 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180 | NoBreak |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transmissivity | ASTMD1003 | 87.0to91.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating 5 | 1.6mm | UL94 | HB | |
| 3.2mm | UL94 | HB | ||
| BurningBehav.at1.6mmnom.thickn. | 1.60mm,UL | ISO12102 | HB | |
| Burning Behav.atthicknessh | 3.20mm,UL | ISO12102 | HB | |
| Oxygenindex | ISO4589-22 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.