Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 水平方向 | | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 1h | | 1800 | Mpa |
| elongation at yield | | | 9.6 | % |
| Tensile modulus | | | 2600 | Mpa |
| Tensile yield strength | | | 63 | Mpa |
| elongation | Break | | 29 | % |
| Charpy impact strength | 23℃ | | 200 | KJ/m |
| Charpy impact strength | 23℃ | | 5.5 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Combustion rate | 1.6mm | | HB | CLASS |
| Hot deformation temperature | 1.80MPa | | 105 | °C |
| Vicat softening temperature | 50℃/h50n | | 150 | °C |
| melting point | 10℃/min | | 167 | °C |
| Coefficient of linear expansion | 水平方向 | | 1.1 | E-4/℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | | 1E+13 | Ohm |
| Dielectric strength | | | 40 | KV/mm |
| Dielectric constant | 100HZ | | 3.8 | |
| Volume resistivity | | | 1E+13 | Ohm |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Loss angle | 100HZ | | 10 | |
| Oxygen index | | | 15 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | | | 0.8 | % |
| Melt index | 220℃/10kg | | 7.5 | CM |
| Density/specific gravity | | | 1400 | kg/cm |
| Moisture absorption rate | | | 0.2 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.