Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | 3.00 mm | | 0.30 到 0.80 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | | ISO 527-2 | 140 | Mpa |
| Tensile strain | Break | ISO 527-2 | > 3.0 | % |
| Bending modulus | | ISO 178 | 8400 | Mpa |
| Bending stress | | ISO 178 | 190 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 170 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 1.0E+15 | ohms |
| Volume resistivity | | IEC 60093 | 1.0E+14 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 100 | °C |
| drying time | | | 3.0 | hr |
| Processing (melt) temperature | | | 170 到 200 | °C |
| Mold temperature | | | 60 到 100 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.