POM Delrin® 127UV NC010 DUPONT USA

131

Unit Price:
$8153 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
24MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Low wear Photostability Low volatility
Application Areas:Plate Automotive sector Automotive interior parts Automotive Interior Parts Profile
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Density/specific gravity		ISO1183	1.42	g/cm³
Melt mass flow rate	190°C/2.16kg	ISO1133	2.4	g/10min
Melt volume flow rate	190°C/2.16kg	ISO1133	1.90	cm3/10min
Shrinkage rate	TD	ISO294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	2.1	%
Water absorption rate	23°C,24hr	ISO62	0.50	%
	Water absorption rate	Saturation,23°C,2.00mm	ISO62	1.2	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.30	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	3000	Mpa
Tensile stress	Yield	ISO527-2	70.0	Mpa
Tensile strain	Yield	ISO527-2	23	%
Nominal tensile fracture strain		ISO527-2	45	%
Bending modulus		ISO178	2700	Mpa
Bending stress	3.5%Strain	ISO178	80.5	Mpa
Bending stress	Bending stress	--	ISO178	72.0	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	160	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	93.0	°C
Vicat softening temperature		ISO306/B50	160	°C
Melting temperature 2		ISO11357-3	178	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	1.1E-04	cm/cm/°C
AnnealingTemperature			160	°C
AnnealingTime-Optional			30.0	min/mm

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	1E+13	ohms·cm
Relative permittivity	100Hz	IEC60250	3.50
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.40
Leakage Trace Index		IEC60112	600	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of cantilever beam gap	23°C	ISO180/1A	13	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	15	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	350	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	400	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO180/1A	11	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale	ISO2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO2039-2	120

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate 3	1.00mm	ISO3795	28	mm/min
UL flame retardant rating	0.8mm	UL94	HB
UL flame retardant rating	UL flame retardant rating	0.8mm	IEC60695-11-10,-20	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO6452	1.5E-04	g

Supplementary Information	Test Method	Test Result	Unit
Emission	VDA275	<8.00	mg/kg
EmissionofOrganicCompounds	VDA277	16.0	µgC/g
Odor	VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.