POM Delrin® 500P NC010 DUPONT JAPAN
123
- Unit Price:
- $4592 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Aging resistance currency Weather resistance
- Application Areas:Electrical tools Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 1.4 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.40 | % | |
| Shrinkage rate | TD | ISO294-4 | 1.9 | % |
| MD | ISO294-4 | 2.0 | % | |
| Melt mass flow rate | ISO1133 | 15 | g/10min | |
| MediumDensity | 1.19 | g/cm³ | ||
| ThermalConductivityofMelt | 0.24 | W/m/K | ||
| Density/specific gravity | ISO1183 | 1.42 | g/cm³ | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 2800 | Mpa |
| Nominal tensile fracture strain | ISO527-2 | 30 | % | |
| Bending stress | 3.5%Strain | ISO178 | 80.0 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Tensile stress | Yield | ISO527-2 | 71.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 17 | % |
| Tensile modulus | ISO527-2 | 3100 | Mpa | |
| Bending modulus | ISO178 | 3000 | Mpa | |
| Poisson's ratio | ISO527 | 0.35 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 | m²/s | |
| Vicat softening temperature | ISO306/B50 | 155 | °C | |
| Melting temperature 2 | ISO11357-3 | 178 | °C | |
| BallPressure Test | 165°C | IEC60695-10-2 | Pass |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | IEC60243-1 | 44 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| 1MHz | IEC60250 | 3.80 | ||
| Leakage Trace Index | IEC60112 | 600 | V | |
| Dissipation factor | 100Hz | IEC60250 | 9E-03 | |
| 1MHz | IEC60250 | 5.5E-03 | ||
| Surface resistivity | IEC60093 | 4E+14 | ohms | |
| Volume resistivity | IEC60093 | 2E+14 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 280 | kJ/m² |
| 23°C | ISO179/1eU | 320 | kJ/m² | |
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.00 | J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO6603-2 | 2000 | N |
| Unscented Izod impact strength | -30°C | ISO180/1U | 250 | kJ/m² |
| 23°C | ISO180/1U | 280 | kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.0 | kJ/m² |
| 23°C | ISO179/1eA | 9.0 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 9.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 92 | |
| R-Sale | ISO2039-2 | 120 | ||
| Ball pressure hardness | H358/30 | ISO2039-1 | 192 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 0.8mm | UL94 | HB | ||
| 1.5mm | UL94 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 22 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| atomization | F-value(refraction) | ISO6452 | 90 | % |
| G-value(condensate) | ISO6452 | 3.5E-04 | g | |
| Burning rate 3 | 1.00mm | ISO3795 | 20 | mm/min |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.10 | µgC/g | |
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.