Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.54 | g/cm³ |
| Apparent density | | | 0.85 | g/cm³ |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 4.00 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.3 | % |
| Shrinkage rate | MD | ISO294-4 | 1.0 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.90 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 7200 | Mpa |
| Tensile stress | Break | ISO527-2 | 115 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.0 | % |
| Tensile creep modulus 3 | 1000hr | ISO899-1 | 4500 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 161 | °C |
| Melting temperature | | ISO11357-3 | 168 | °C |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Maximum operating temperature - sortcycle operation | | | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+14 | ohms |
| Volume resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 85 | KV/mm |
| Relative permittivity | 1MHz | IEC60250 | 4.10 | |
| Dissipation factor | 1MHz | IEC60250 | 7E-03 | |
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.5 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 50 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 50 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 164 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| AutomotiveMaterials | >1.00mm | FMVSS302 | Passed | |
| ISOType | | ISO9988-1 | POM-K,M-GNR,02-003,GF20 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.