POM KOCETAL® GF705 KOLON KOREA
232
- Unit Price:
- $4000 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High rigidity Filler: Glass fiber reinf
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 10 | g/10min |
| Shrinkage rate | MD | ASTMD955 | 0.50 | % |
| TD | ISO294-4 | 1.2 | % | |
| MD | ISO294-4 | 0.64 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 | % |
| Equilibrium,23°C,60%RH | ASTMD570 | 0.20 | % | |
| Density/specific gravity | ASTMD792 | 1.59 | g/cm³ | |
| ISO1183 | 1.59 | g/cm³ | ||
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 10 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 23°C | ASTMD790 | 7800 | Mpa |
| 23°C | ISO178 | 8700 | Mpa | |
| bending strength | 23°C | ASTMD790 | 220 | Mpa |
| Bending stress | 23°C | ISO178 | 200 | Mpa |
| Tensile strength | Yield,23°C | ASTMD638 | 147 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 140 | Mpa |
| elongation | Yield,23°C | ASTMD638 | 7.0 | % |
| Tensile strain | Break,23°C | ISO527-2 | 3.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 162 | °C |
| Melting temperature | ISO11357-3 | 166 | °C | |
| 166 | °C | |||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 2.5E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 164 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 163 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | ASTMD150 | 3.70 | ||
| Dissipation factor | 1MHz | ASTMD150 | 6E-03 | |
| Surface resistivity | ASTMD257 | 1E+16 | ohms | |
| IEC60093 | 1E+16 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+14 | ohms·cm | |
| IEC60093 | 1E+14 | ohms·cm | ||
| Dielectric strength | ASTMD149 | 19 | KV/mm | |
| IEC60243-1 | 19 | KV/mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 7.5 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 70 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Scale | ASTMD785 | 90 | |
| M-Scale | ISO2039-2 | 96 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.